物理化学综述.docxVIP

脲醛树脂胶粘剂改性研究及其发展前景 尤小虎(特能1001 （西南科技大学,绵阳,621010） 摘要：脲醛树脂胶粘剂具有胶合强度高、固化快、胶层无色等优点，但是脲醛（UF）胶粘剂与其他胶种相比还存在耐水性差、固化后胶层脆性大、耐老化性能不佳和游离甲醛含量高等缺点。所以研究在三聚氰胺，聚乙烯醇，苯酚-PVA，等对脲醛（UF）树脂进行改性后的粘接强度、耐水性、抗老化性、固化时间，等的变化及其研究进展有重大意义，并阐述了在以后脲醛树脂的发展前景。 关键字：脲醛树脂；粘胶剂；改性；进展；发展前景 中图分类号： TB322 文献标识码： A Urea-formaldehyde resin adhesive modified its development prospects XiaoHu YOU （Southwest University of Science and Technology,MianYang，621010） Abstract：Urea-formaldehyde resin adhesive with high bonding strength, fast curing adhesive layer colorless etc ,Urea-formaldehyde (UF) adhesives and other types of plastic compared to poor water resistance, poor brittle adhesive layer after curing, aging resistance and free formaldehyde content of the disadvantages. So research in the melamine, polyvinyl alcohol, phenol-PVA, such as the strength of adhesion after the modified urea-formaldehyde (UF) resins, water resistance, aging resistance, curing time, such as changes in its research progress has great significance, And urea-formaldehyde resin in the future development prospects. Keywords：Urea-formaldehyde resin; Adhesives; Modified; Progress; Development prospects 前言 脲醛（UF）树脂胶粘剂被广泛应用于木器加工、室内装修人造板材[1]等，UF树脂胶粘剂是我国木材工业用量最大的合成树脂胶粘剂，占木材加工使用胶粘剂的60%之多，占人造板用胶的90%左右[2]。其主要原因在于UF树脂具有较高的胶接强度、高的耐冷水性能、中等耐热水性能、固化迅速、等优点，此外其制造工艺简单易于得到[3]，并且其制造原料来源广泛、价格低廉，它是合成树脂胶粘剂中价格最低的。但是其还存在一些缺点这就需要我们去进行改进以提高它 的价值。其主要存在的缺点在于耐水性差、耐老化性能差、游离甲醛含量高等，所以通过对其改性研究得到更好的胶粘剂。本文主 要通过介绍加入不同的改性剂对UF树脂胶粘剂的影响，以及在今后还需要做得一些改进，并简单的介绍一下UF树脂胶粘剂在以后的发展前景。 加入不同改性剂对脲醛（UF）树脂影响 1.1降低脲醛（UF）树脂游离甲醛改性剂 甲醛释放的主要原因［4］是：①在合成树脂的初期加成反应阶段，由于可逆反应造成的未能彻底反应的游离甲醛；②在固化和缩聚反应中生成甲醛键及羟甲基热压阶段的分解；③在热压后残留的甲醛键和羟甲基在环境的作用之下的分解。在合成实验中可得知游离甲醛含量影响因素重要性的顺序为：甲醛/尿素摩尔比尿素分批加入比例三聚氰胺加入量三聚氰胺加入时间[5]。尿素、鞍、苯胺、己内酰胺、丙稀酰胺、对甲苯磺酰胺、部分铵盐等胺类化合物，硫代硫酸钠、二亚硫酸钠、硫脲，以及间苯二酚、聚乙烯醇等都是常用的单一甲醛捕捉剂。下面简单介绍一下国内外研究比较多的几种单一类和复合类改性剂。 1.1.1三聚氰胺 三聚氰胺是改善低摩尔比脲醛树脂胶粘剂最常用的改性剂。Sum in K im［6］研究表明：MF共混改性的UF 胶粘剂压制的MDF的游离甲醛的释放量得到明显的降低，其主要是因为甲醛与三聚氰胺比与尿素更容易发生加成反应。在国内的实验研究表明：在UMF树脂胶粘剂，在尿素与甲醛的摩尔比相同时，随着三聚氰胺加入量的增加，游离醛含量降低，