掺石灰粉对粉煤灰再生混凝土抗冻性能的影响.pdfVIP

文章编号：1007—046X(2013)0卜0040—03 生态建材 掺石灰粉对粉煤灰再生混凝土抗冻性能的影响 Influence of Lime Powder on Freezing—Thawing Performance of Fly Ash Recycled Concrete 朱 涛，吴相豪，袁 潘 (上海海事大学 海洋环境与工程学院，上海 201306) 摘 要：采用快速冻融试验方法，研究了石灰粉掺量对粉煤灰再生混凝土抗冻性能的影响规律。试验结果表明： 石灰粉等量取代部分粉煤灰对粉煤灰再生混凝土抗冻性能有一定的影响，随着石灰粉等量取代粉煤灰率 的增加，粉煤灰再生混凝土抗冻性能是先增强后减弱，掺适量的石灰粉可以改善粉煤灰再生混凝土的抗 冻性能，石灰粉最佳取代率为10％左右。 关键词：粉煤灰；石灰粉；再生混凝土；抗冻性能 中图分类号：TU528．2 文献标志码：A Abstract：The influence of lime powder on freezing．thawing performance of fly ash recycled concrete was investigated by accelerated freezing and thawing test．The results showed that：substituting lime powder for part of isometric fly ash has a certain influence on the frost resistance of fly ash recycled concrete．frost resistance of recycled concrete increased firstly and then decreased with the ratio of lime powder raising，thence，an appropriate amount of lime powder could improve the frost resistance of recycled concrete．the optimum replacement ratio iS about 1 O％． Kev words：fly ash；lime dust；recycled concrete：freezing and thawing 0 前 言 1 试 验 在寒冷地区，冻融是主要的环境荷载，是引起混凝土 1．1 原材料及配合比 结构破坏的主要因素。抗冻性能是评价混凝土结构耐久性 1．1．1 原材料 的重要指标之--[1-3]。再生混凝土是一种环保型建筑材料， 水泥：P．O 42．5海螺牌水泥。粉煤灰：Ⅱ级粉煤灰， 越来越多地应用于建筑工程领域，有必要开展再生混凝土 45 m筛的筛余为l4．8％，需水量比为98．6％，烧失量为 抗冻性能的研究。冯嘉等[ 1等研究了矿物掺合料等因素对 5．79％。石灰粉：上海金山生产的生石灰，在室内空气中 再生混凝土抗冻性能的影响，结果表明掺普通矿粉的再 自然熟化而成的粉末，用25 m方孔筛过筛，取粉末装 生混凝土比掺粉煤灰的再生混凝土抗冻性好，硅灰对提高 入防潮塑料瓶备用(有效钙含量≥85％)。再生粗集料： 再生混凝土抗冻性有明显作用。王军强等【 】研究了再生混 选用路面废弃混凝土，人工破碎后，再除杂、筛选、分级、 凝土的基本力学性能和抗冻耐久性能，结果表明采取外 清洗得到粒径在5～20 mm范围的粗集料。细集料：选用 掺粉煤灰和引气剂配置的再生混凝土具有较强的抗冻性能， 细度模数为2．82的河砂。水：采用自来水。 可以满足寒冷区域环境下使用。理论上讲，石灰是一种以 1．1．2 配合比 氧化钙为主要成分的气硬性无机胶凝材料，具有一定的