D36钢在海洋环境中的腐蚀疲劳裂纹扩展研究-船舶与杨海洋结构物设计制造专业毕业论文.docxVIP

D36钢在海洋环境中的腐蚀疲劳裂纹扩展研究Study D36钢在海洋环境中的腐蚀疲劳裂纹扩展研究 Study on the Corrosion Fatigue Crack Growth of D36 Steel in Seawater Abstract D3 6 steel，being a material widely used in offshore structures，often suffers severe corrosion fatigue damage during a structure’S service time．So．studying on the CFCG of D36 steel in seawater iS significant．Among current research on the CFCG behavior of steel structures，various regression based on Paris Equation have been commonly carried o此yet very few has discussed the mechanism of crack growth．Besides，among research on the mechanism of CFCG，yet very few have given t