《CR、NR共混体系的导电性能的研究》-毕业论文（设计）.docVIP

l CR/NR共混体 系的导电性 能的研究 l CR/NR共混体 系的导电性 能的研究 CR/NR共混体系的导电性能的研究 摘要： 本论文采用天然橡胶和氯丁橡胶共混并用胶为基体，研究了并用胶在室温下导电性能和力学性能随乙炔炭黑填充量的变化关系、并用胶在室温下导电性能和力学性能随CR/NR配比不同的变化关系。 结果表明：随着乙炔炭黑用量的增加，并用胶的体积电阻率逐渐减小，导电性能增强，但在乙炔炭黑用量超过60份后，体积电阻率变化变缓。随着CR/NR配比中NR用量的增加，并用胶的电阻率先减小后增加，导电性能先增强后减弱。 关键词：乙炔炭黑，并用胶，导电橡胶，体积电阻率  The research of electrical property of the CR and NR blend Abstract: In this thesis,the substrates is natural rubber and chloroprene rubber.Studied the changes in the relationship of electrical properity and mechanical properties with the different amount of acetylene black.Studied the changes in the relationship of electrical property and mechanical properties with the different ratio of natural rubber and chloroprene rubber. The result shows that the blend rubber’s volume resistivity reduce gradually and electrical property increase gradually with increase of the amount of acetylene black.But the volume resistivity change smoothly when the amount of acetylene black more than sixty.The blend rubber electrical property first increased and then decreased. Keywords: acetylene black,blend rubber,conductive rubber, acetylene black 目录 TOC \o 1-3 \u 1文献综述 1 1.1导电橡胶概述 1 1.1.1导电橡胶的组成 1 1.1.2导电橡胶的导电机理 3 1.1.3导电橡胶导电性能的影响因素 4 1.1.4导电橡胶的应用 5 1.2 NR与CR的概述 7 1.2.1天然橡胶 7 1.2.2氯丁橡胶 9 1.3研究的目的及意义 10 2 实验部分 11 2.1实验原料 11 2.2实验设备 11 2.3实验配方 12 2.4 实验工艺 13 2.5样品制备 14 2.5.1混炼 14 2.5.2硫化 14 2.5.3制样 15 2.6性能测试实验 16 2.6.1体积电阻率 16 2.6.2拉伸性能 17 2.6.3抗撕裂性能 17 2.6.4硬度 18 3 测试结果分析 19 3.1导电性 19 3.2拉伸性能 21 3.3抗撕裂强度和硬度 24 3.4并用橡胶导电性能的影响因素 25 3.4.1乙炔炭黑的用量对并用胶导电性能的影响 25 3.4.2炭黑结构性对橡胶导电性能的影响 26 3.4.3橡胶基体对炭黑分散状态及材料电性能的影响 26 3.4.4加工工艺对炭黑分散状态和材料电性能的影响 26 4 结论 27 参考文献 28 致谢 29 1文献综述 1.1导电橡胶概述 近年来，导电高分子材料的研究取得了较大的进展，科学家对其合成、结构、导电机理、性能、应用等方面经过多年研究，已经使其成为一门独立的学科。导电高分子材料由于其易成型、质量轻、易于加工等优点已经在各个领域有了广泛的应用。 导电高分子材料可按其导电性和组成来分。按导电性能（电阻率的大小）可分为半导体材料、防静电材料、电阻体材料、电极材料、高导体材料五类。按组成分为结构型和复合材料型两大类，后者又可以分为抗静电型、表面处理型和导电填料型。复合导电高分子材料是材料领域的一大体系，由于它有许多优异特性，已经在许多领域中得到应用。 导电橡胶是填充型导电高分子的一大类。它主要是将导电性材料与