异型坯预制裂纹试验研究.pdfVIP

2007 中国钢铁年会论文集 异型坯预制裂纹试验研究 霍喜伟 孙丽新 袁鹏举 张 婕 李春传 （莱芜钢铁集团有限公司，莱芜 271104 ） 摘 要 本文通过对莱钢 H 型钢腹板裂纹组织的金相和扫描电镜分析发现，在裂纹周围的组织中存在大量异质颗 粒。为了弄清此类异质颗粒的性质及其与裂纹之间的联系，以及具有该相同特征的裂纹组织的形成过程，特设计预 制裂纹实验方案进行验证，通过试验研究，发现了异质颗粒的性质及其与裂纹之间的联系，判断出具有该相同特征 的裂纹组织的形成过程，总结出了影响异质颗粒形成及大小的主要因素。 关键词 裂纹 预制 异质颗粒 析出物 The Test Research of Shaped Blank Crack Huo Xiwei Sun Lixin Yuan Pengju Zhang Jie Li Chunchuan （Laiwu Steel Group,Ltd., Laiwu, 271104 ） Abstract In the metallographic and SEM analysis to the web crack of H beam, we found that there are lots of heterogeneity particulates round the crack. In order to know the character of them, the contact between them and the crack, and their forming process, we designed a special experiment- prefabricate crack in the shaped blank. In the experiment, we found the character of the heterogeneity particulates and the contact between them and the crack, and their forming process, summarized the main factors to influence their forming process and size. Key words crack, prefabricate, heterogeneity particulates, deposition 1 引言 莱钢大 H 型钢异型坯连铸和轧制生产线的顺利投产，使莱钢的产品结构、装备结构和工艺结构调整迈 出了关键性的一步。由于该生产线设备复杂，控制难度大，生产过程中必然会遇到一系列问题。其中，腹板 裂纹问题较为突出，它已经成为困扰大 H 型钢质量稳定的重要问题之一。围绕腹板裂纹产生的原因、形成 机理和解决措施作了大量的工作，而其中之一便是 H 型钢腹板裂纹周围异质颗粒形成机理的研究。 2 腹板裂纹的宏观和微观形貌特征 在对腹板裂纹的研究过程中，通过对几个月来上千个裂纹 形貌的观察发现，这些裂纹在宏观上具有某些共同的特征，如 裂纹沿轧制方向分布于腹板中心或偏离中心1/2 处；裂纹深度 0.2～0.5mm，个别严重的到1mm，裂纹长度100～2000mm ， 有的达到5000mm；同时还对这些腹板裂纹进行了取样分析， 光学显微镜观察表明在裂纹周围有明显的脱碳层，裂纹表面有 氧化铁。还发现在这些腹板裂纹样品中，约 90% 的裂纹周围 存在细小的异质颗粒，上述异质颗粒主要分布在脱碳层，并深 入到基体内部，金相图片如图1 所示。 图 1 金相图 在扫描电镜下观察到裂纹周围有大量细小的球形异质颗 Fig.1 Constitution diagram 粒，其尺寸大部分小于1 µm ，个别达到 5 µm 。