实训基地 技术咨询与答疑 一种PLLA用新型成核剂.pptxVIP

一种PLLA用新型成核剂高分子教研室一种PLLA用新型成核剂Nonisothermal crystallization of PLLA/NA compositesNA含量降温速率Tc（℃）?Hc （J/g）Tm（℃）?Hm（J/g）0 %wt5℃/min94.84.6168.337.610℃/min93.80.3168.527.20.1 %wt5℃/min95.56.0169.139.510℃/min94.33.7168.431.90.2 %wt5℃/min128.623.7169.441.010℃/min119.513.1166.941.40.3 %wt5℃/min131.037.3169.143.610℃/min123.934.1169.540.30.4 %wt5℃/min131.148.3169.449.510℃/min124.334.2168.643.10.5 %wt5℃/min132.048.9169.950.010℃/min124.639.2168.741.4Isothermal crystallization of PLLA/NA compositesTc (oC)nk (min-n)t0.5 (min) Neat PLLA1202.81.66×10-38.701252.54.27×10-418.41302.51.86×10-425.81352.41.55×10-434.21402.43.09×10-565.0PLLA/OA 0.2wt%1202.28.41×10-10.9151252.06.68×10-11.021302.13.97×10-11.301352.12.90×10-11.501402.63.98×10-23.01PLLA/OA 0.3wt%1202.41.990.6391252.61.390.7651302.69.67×10-10.8801352.64.34×10-11.191402.71.15×10-11.96PLLA/OA 0.5wt%1202.42.340.6051252.51.760.6871302.61.1880.8111352.75.70×10-11.081402.91.36×10-11.76AcknowledgementsMOENSFCThank you for your attention!