铟对可溶解合金溶解性能的影响.docVIP

铟对可溶解合金溶解性能的影响 摘 要 本文以铝，其他活化元素，铟为原料，按照一定的质量分数进行配比，利用高温熔融工艺，得到一种既具有一定溶解能力，又具有一定力学性能的新型高强铝合金材料。通过溶解实验，利用溶解曲线，成功得出铟的最佳加入量，同时通过X射线衍射（XRD)分析研究了高强铝合的溶解机理；结果表明，铟的加入量与溶解性能并不成正比，铟的加入量对铝合金的溶解速率的影响有个临界点，当铟的量为0.4wt%时，溶解速率达到最大，以后随着铟的加入量的增加，溶解性能的改变并不大，而对于溶解机理，主要是因为形成了金属件化合物。 关键词：可溶解合金材料，铝合金，溶解性能，溶解机理 Study on Indium of soluble aluminum dissolved performance impact ABSTRCT A new aluminum alloy material with the property of mechanical and dissolve was fabricated through high temperature melting process. The best additives quantity of In was get through dissolvable experiment and dissolvable curve.Meanwhile the reaction mechanism of dissolvable aluminum alloy material was investigated by X-ray diffraction analysis (XRD) in detail.The result suggested that the amount of additive In and the dissolvable property was not in diret ratio. As the increase of the amount of In, the dissolvable rate reached to an limitation.When the amount of In was 0.4wt%, the dissolve rate reached to the highest.however, with the increase of In above 0.4wt%, the dissolve rate did not change too much.Also the formation of intermetallic compounds attribute to the dissolvable of the aluminum alloy KEY WORDS: the dissolvable material, dissolve property, aluminum alloy, dissolve mechanism 目 录 TOC \h \z \t 标题 1,2,标题,1,副标题,3 摘要 I ABSTRCT II 1 文献综述 1 1.1 引言 1 1.2 铝合金材料介绍 1 1.2.1 铝合金简介 1 1.2.2 物理特性 2 1.3 铝与水的反应 2 1.4 金属铟 3 1.5 国内外研究现状 4 1.6 可溶解铝合金材料的制备方法 5 1.6.1 高温熔融法 5 1.7 关于可降解合金溶解机理的探讨 6 1.7.1 不同合金元素溶解分析 6 1.7.2 对于溶解机理的不同观点 8 1.8 本研究的目标，内容及意义 10 1.8.1 研究目标 10 1.8.2 研究内容 10 1.8.3 研究意义 11 2.1 主要原料和设备 12 2.1.1 主要原料 12 2.1.2 主要实验设备 12 2.2 试验配方选定与理论依据 13 2.2.1 配方设计 13 2.2.2 理论依据 13 2.3 实验过程 14 2.3.1 总体工艺过程 14 2.3.2 前期实验过程 14 2.3.3 金属铟含量对材料性能影响的实验过程 15 3 结果与讨论 16 3.1 金属元素铟对可溶解铝合金性能的影响 16 3.1.1 不同温度下金属元素铟对溶解性能的影响 16 3.1.2 化学热力学分析 18 3.2.2 XRD测试结果与分析 19 4 结论 20 致谢 21 参考文献 22 1 文献综述 1.1 引言 材料，能源，信息作为21世纪的三大支柱，