亚共析钢连续加热奥氏体化模型 杨阿娜.docxVIP

亚共析钢连续加热奥氏体化模型 杨阿娜 亚共析钢连续加热奥氏体化模型lowbar;杨阿娜 《热加工工艺》2021年11月第42卷第22期 亚共析钢连续加热奥氏体化模型 (宝山钢铁股份有限公司研究院, 上海202100) 要：研究了原始组织为铁素体和珠光体的亚共析钢奥氏体转变动力学，并根据Cahn 的晶界形核理论建立了一 个包括组织、成分和加热速度等参数在内的模型。实验结果和理论预测结果表明，当不考虑Mn 对转变动力学影响时，实验结果与模型计算结果吻合良好。 关键词：亚共析钢；奥氏体化；模型中图分类号：TG111 文献标识码：A 文章编号：1001-3814(2021)22-0055-04 Modelling of Austenite Transformation of Hypo -eutectoid Steel During Continuous Heating YANG Ana (ResearchInistitute of Baoshan Iron Steel Co., Ltd., Shanghai 202100, China) Abstract ：The kinetics of austenite transformation of hypo-eutectoid steel with initial microstructure of ferrite plus pearlite during continuous heating were studied. A theoretical model for incorporating microstructure, chemical composition and heating rate etc, was constructed on the basis of Cahns grain boundary nucleation theory. The experimental results show that a good agreement between them is eventually obtained without considering the effect of Mn on the transformation kinetics. Key words ：hypo-eutectoid steel; austenitization; modelling 钢在热处理过程中不可避免地发生奥氏体化，与奥氏体的分解相比，奥氏体的形成没有引起足够的重视，原因可初步归因于钢的淬透性在决定其性能方面的重要性。正如Law 等[1]所讨论的，奥氏体的形成与它的分解过程的差异主要体现在两个方面。在奥氏体分解过程中，随着过冷度的增加，热力学驱动力增大而原子的扩散速度受到抑制，这导致了典型的C 曲线型转变动力学行为。相反，在加热过程中，无论驱动力还是原子的扩散速度均随温度的升高而增大，因此转变动力学曲线上没有“鼻子”。此外，冷却过程都是从均匀的奥氏体开始，其动力学过程可很好地用成分和奥氏体晶粒大小加以描述，而在奥氏体形成过程中，由于原始组织是多种多样的，这种简化是不可能的。 最近，由于低碳钢的广泛应用使得原始组织为铁素体和珠光体的钢的奥氏体形成动力学引起了人们的广泛关注。Datta 等[2]研究表明，低温时奥氏体的径向长大可由简单的抛物线规律加以描述。在高温 时，没有形核发生，长大速度趋向于常数。奥氏体的形核优先在位于铁素体晶界处的Fe 3C 粒子处形成。 Gaude-Fugarolas 等[3]根据经典形核理论和扩散控制 长大方程，考虑到钢的成分、原始组织和热历史，建立了亚共析钢奥氏体化模型。鉴于此，本文主要研究了原始组织为铁素体和珠光体的亚共析钢的奥氏体转变动力学，并根据Cahn 的晶界形核理论建立了一个包括组织、成分和加热速度等参数在内的模型。 1.1基本假设 (1)铁素体和珠光体团假定为正十四面体；(2)形核优先发生在晶界，晶棱和晶角处，因为 这些位置处的能量较晶粒内部高，如图1所示。 收稿日期:2021-03-11 作者简介:杨阿娜(1979-), 女, 山东威海人, 硕士研究生, 主要研究方向 为热轧产品工艺研究; 电话:[1**********]; 图1铁素体和珠光体团三种不同形核位置示意图 E-mail:yangan@ Fig.1Schematic diagram showing three different nucleation s