二氧化钛胶粒嵌入超细层状钛酸盐制备金红石型氧化钛纳米纤维(中英文混合版).pdfVIP

J. Yang et al. / Materials Letters 61 (2007) 1855-1858 翻译者：向兴龙 第 1 / 11 页 原 作 者 ： Juan Yang （杨娟） , Qinqin Liu （刘芹芹） , Xiujuan Sun （孙秀娟） Preparation of rutile TiO 2 nanofibers by TiO 2 sol intercalation of ultrafine layered titanate 二氧化钛胶粒嵌入超细层状钛酸盐制备金红石型氧化钛 纳米纤维 Juan Yang （杨娟）, Qinqin Liu （刘芹芹）, Xiujuan Sun （孙秀娟） 江苏大学材料科学与工程学院，江苏镇江，邮编： 212013 2006 五月 17 日收到； 2006 年 7 月 23 日接受； 2006 年 8 月 15 日开始在线使用 Abstract To prepare TiO2 intercalated tetratitanate, TiO2 solution and ultrafine layered titanate K2Ti4O9 obtained via solid-state reaction by using nanometer-sized TiO2 as raw material were used as guest and host materials respectively. The structure and morphology of the resulting samples were characterized by XRD and TEM experiments. It was found that during the intercalation process, the interlayer distance was expanded step-by-step and the interlayer structure of titanate might be destroyed and degraded to slits by prolonging the solution intercalation time. Rutile TiO2 nanofibers with the average size of 5 ×50 nm were obtained at room temperature while the duration time was prolonged to 72 h. ? 2006 Elsevier B.V. All rights reserved. 摘要：为了制备二氧化钛嵌入钛酸盐（ tetratitanate）材料，用二氧化钛溶胶和超 细层状 K2Ti4O9 分别作为主体和辅体原料进行固相反应得到纳米二氧化钛。对 试样的结构和形貌进行了 XRD 和 TEM 表征。研究结果表明，嵌入过程中，延 长嵌入时间， 层间距离会逐步增大， 钛酸盐夹层结构被破坏然后微裂纹空隙中被 微小粒子嵌入。室温下持续 72 小时可得到平均尺寸约为 5×50nm 的金红石型 TiO2 纳米纤维。 ? 2006 Elsevier B.V 保留所有权利。 Keywords: Rutile TiO2 nanofiber; Ultrafine layered titanate; Sol intercalation 关键词：金红石纳米纤维；超细分层钛酸盐；溶胶插入法 1. Introduction Recently, the pillaring of sol particles into layered inorganic solids has received considerable atten