铝合金化学镀镍的研究论文.docVIP

PAGE PAGE II 题目：铝合金化学镀镍的研究 　　　　　　　　　　　　　　　　　　　 Ⅰ 多用途化学镀镍溶液的研究 摘 要 本文主要研究碱性化学镀镍后在酸性镀镍的工艺，通过正交试验选出一种较好的镀液配方，讨论了分别讨论络合剂、稳定剂、缓冲剂、温度及pH 值的影响，检测了镀层的性能。 本次正交试验表明，对于这种金属可行的方案是：硫酸镍25g/L，次亚磷酸钠25g/L，柠檬酸钠20g/L，碘化钾10g/L，乙酸钠20g/L，施镀温度75℃，pH=5，施镀时间1h，并对其镀层进行了研究。通过表征镀层的外观、耐蚀性和孔隙率指标来表明镀层已经达到要求。 关键词：镍磷合金；化学镀镍；镀层 Ⅱ Multi-purpose Solution of Chemical Nickel Abstract In this paper, the author studied a multi-purpose electroless nickel plating solution, so that it can be used for a variety of substrate materials. Ascertain a better solution formula by Orthogonal design. and then study the appearance, corrosion resistance, porosity and other performances of chemical nickel coating. The test showed that the feasible program for these three metals are: nickel sulfate 25g/L, sodium hypophosphite 25g/L, sodium citrate 20g/L, potassium iodide 10g/L, ammonium acetate 20g/L, plating temperature of 75℃, pH=5, plating time 1h, and its deposits were studied. It is characterized by the coating of the appearance, corrosion resistance and porosity, and than use it to show that the coating has reached the requirements. Key Words: nickel-phosphorus alloy;Chemical nickel plating;Coating Ⅳ 目 录 TOC \o 1-3 \u 1 绪论 1 1.1研究背景 1 1.2化学镀镍概述 3 1.2.1化学镀Ni-P 3 1.2.2化学镀镍溶液的组成及其作用 4 1.3化学镀镍动力学反应机理 6 1.3.1化学镀Ni-P合金的机理 6 1.3.2原子氢理论 7 1.3.3电化学机理 8 1.3.4 化学镀镍溶液各组份的剖析 8 1.5化学镀的国内外应用现状 11 1.5.1化学镀镍层的性能 11 1.5.2化学镀镍磷层的应用现状 12 1.6 研究目的与意义 14 2 实验部分 16 2.1 实验药品 16 2.2 实验仪器 16 2.3 工艺流程 16 2.4.1化学镀镍液的配制 17 2.4.2施镀过程 17 2.5 镀后检测 19 2.5.1外观检测 19 2.5.2耐蚀性检测 19 2.5.3孔隙率检测 19 3 结果与讨论 20 3.1镀前预处理 20 3.2络合剂的影响 20 3.4 稳定剂的影响 21 3.5缓冲剂的影响 22 3.6温度的影响 22 3.7 pH的影响 23 3.8镀层表面检测 23 3.9耐蚀性的检测 24 3.10孔隙率的检测 24 参考文献 26 致 谢 28 毕业设计（论文）知识产权声明 29 毕业设计（论文）独创性声明 30 PAGE 16 1 绪论 1.1研究背景 化学镀镍是一种比较新的工艺技术。化学镀镍的历史与 电镀相比，比较短暂在国外其真正应用到工业仅仅是70年代末80年代初的事。1844年，A.Wurtz发现金属镍可以从金属镍盐的水溶液中被次 磷酸盐还原而沉积出来。 化学镀镍技术的真正发现并使它应用至今是在1944年，美国国家标准局的A.Brenner和G.Riddell的发现，弄清楚了形成涂层的催化特性，发现了沉积非粉末状镍的方法，使化学镀镍技术工业应用有了