(2885)--利用SAP颗粒对植生泡沫混凝土28_d龄期内碱度的调控研究.pdfVIP

利用SAP 颗粒对植生泡沫混凝土 28 d 龄期内碱度的调控研究 摘 要： 采用固液萃取法，研究了28 d 龄期内植生泡沫混凝土碱度控制方法。采用SAP 颗粒作为降碱物质的存储载体，利用其 在胶凝材料水化过程中的液相反渗，缓释降碱物质，维持泡沫混凝土内的低碱度。研究采用降碱物质固相干混、不同浓度降碱溶 液SAP 颗粒预吸等方法制备泡沫混凝土，测试28 d 龄期内pH 值。SAP 颗粒预吸5% 以下浓度硼酸溶液后，对泡沫混凝土降碱效 28 d 内pH 值稳定在9。 果较好， 关键词： 植生；泡沫混凝土；SAP 颗粒；碱度 中图分类号： TU528.2 文献标志码： A 文章编号： 1002-3550 （2020）06-0160-03 LI Xiao，ZHAO Jingwen （School of Materials Science and Engineering，Shenyang Jianzhu University，Shenyang 110168，China） Abstract:The solid-liquid extraction was used to study controlling means of alkalinity for planting foamed concrete in 28 d.The SAP particles were used to store alkalinity reducing material.The liquid would ooze from SAP particles in the hydration process of cementing material and the low alkalinity would be maintained in foamed concrete.The alkalinity reducing material was used to dry mix or absorbed by SAP particles before mixing.The pH vale of foamed concrete was tested in 28 d.When the solution of boric acid was no more than 5% ， the pH vale of foamed concrete was about 9. Keywords:planting ；foamed concrete；SAP particles；alkalinity 0 引言 1 原材料与试验方法 现今，植生混凝土主要是由大骨料制备，具有大尺寸 1.1 原材料 孔隙率高、可填充植生基材、能使植物正常生长性能的混 研究中采用北极熊硫铝酸盐42.5 级水泥，1 d 抗压强 凝土[1]。此类植生材料存在的问题就是内部碱度较高，不适 度30.0 MPa，28 d 抗压强度45.0 MPa；沈海热电厂II 级粉煤 灰；80 目SAP 颗粒，吸水倍率800 倍；瓦克5 044 N 可分散 [2] [3] 于植物生长 何池全等 提出植生混凝土孔隙pH 值需降 。 性胶粉； 30%浓度双氧水；绿森MP-50H 稳泡剂；3~5 mm 玄 到11 左右才能使植物生长，而现有的研究表明孔隙pH 值 武岩纤维短切丝；硫酸铜、硫酸亚铁、氯化铁、柠檬酸、硼酸、 最好能降到9 。本研究所涉及的采用泡沫混凝土体系植生