(2903)--利用未淡化海砂配制超高性能混凝土的研究.pdfVIP

2019 年第5 期 混凝土与水泥制品 2019 No.5 5 月 CHINA CONCRETE AND CEMENT PRODUCTS May 利用未淡化海砂配制超高性能混凝土的研究 摘 要：利用未经淡化处理的海砂配制了超高性能混凝土（UHPC ） ，并研究了不同水胶比、砂胶比、胶凝材料体 系、钢纤维掺量、养护制度对海砂UHPC 的流动度、抗压强度、抗折强度的影响。 试验结果表明：海砂UHPC 的最优 水胶比、砂胶比和纤维体积掺量分别为 0.16 、1.0 和 1.5% ，最佳的胶凝材料体系组成是水泥、降黏剂和硅灰分别70% 、 15%和 15% ，最合适的热养护制度是 70 ℃蒸汽养护；按照上述参数配制的海砂 UHPC 力学性能完全符合相关标准 的要求。 关键词：海砂；超高性能混凝土；钢纤维；养护制度；降黏剂 Abstract: Ultra-high performance concrete (UHPC) was prepared by mixing with untreated sea sand, and the effect of different W/B, sand -binder ratio, cementitious systems, steel fiber volume contents, curing schedules on the fluidity, compressive strength and flexural strength of UHPC with untreated sea sand are studied. The results show that: the optimum W/B, sand-binder ratio and steel fiber volume content of UHPC made with untreated sea sand are 0.16, 1.0 and 1.5% respectively; the optimum cementitious system is composed of 70% cement, 15% viscosity reducer, and 15% silica fume; the most suitable curing schedule is steam curing in the temperature of 70 ℃ ; and according to the above parameters, the mechanical property of UHPC with untreated sea sand can meet the requirements of current national standard. Key words: Sea sand; Ultra-high performance concrete(UHPC); Steel fiber; Curing schedule; Viscosity ruducer 中图分类号： 文献标识码： doi:10.19761/j.1000-4637.2019.05.001.04 TU528.45 A 0 前言 凝土进行系统试验研究。 超高性能混凝土 （Ultra -High Performance 1 原材料与试验方法 ， ）是一种高强度、高韧性、高耐久的 原材料 Concrete UHPC 1.1 超高强水泥基材料[1-4] ，其基本配制原理是：通过提 水泥为 · 级水泥， 抗压强度为