(2893)--利用堆积密度优化混凝土配合比的研究.pdfVIP

商品混凝土 实践技术 Beton Chinese Edition —— Ready-mixed Concrete 2020 年第 4 期 利用堆积密度优化混凝土配合比的研究 ［摘 要］ 本文针对商品混凝土常用 C30 配合比，采用粗细骨料紧密堆积和部分石粉替代细骨料的方法，实现混 凝土最密实结构。试验表明，将原级配石子进行筛分并进行复配实现紧密堆积可减少 11kg 胶材用量，混凝土强度 与和易性不出现变化。采用石粉替砂的方式实现细骨料紧密堆积，可使混凝土单方胶材用量降低 30kg 。配合比优 化后减少了胶凝材料用量，大幅减少了水化热，降低了生产成本。 ［关键词］ 堆积密度；商品混凝土；配合比优化 Study on optimization of ready-mixed concrete proportion by using stacking density Wu Wei, Luo Xiaodong, Tao Jun, Xiao Shiyu, Wu Tao (Chengdu Jiangong Seller Concrete Co., Ltd., Chengdu 610015) Abstract: In this paper, the common concrete C30 mix proportion will be optimized by using dense packing density of coarse and fine aggregate or the replacement of fine aggregate with lime stone powder. The experiment shows that 11kg binder can be reduced by sieving and compounding the original coarse aggregate, and the strength and workability of 3 concrete do not change. 30kg/m cementious materials can be reduced by using the replacement of fine aggregate with lime stone powder. Using the optimal mix proportion, the heat of hydration and the cost of production will be greatly reduced by the minimal amount of binder. Key words: stacking density; ready-mixed concrete; mix proportion optimization 0 前言 中Ⅱ砂与中 Ⅲ 砂。中 Ⅱ细度模数 2.8 ，含泥量 3.2% ； 中Ⅲ 细度模数 2.2 ，含泥量 5.6% 。 混凝土单方成本一直是各工程与商品混凝土企业关 （5 ）石子：成都建工赛利混凝土有限公司 5 ～ 注的热点，特别是目前水泥、砂石等受环保压力与运输 31.5mm 连续级配碎石，针片状含量 1.1%，压碎值 限制，混凝土单方成本不断攀升。本文针对常用强度等 3 3 5.7%，表观密度 2840kg/m ，堆积密度 1617kg/m ，空 级 C30 在不改变原有材料品质的条件下，对粗细骨料