　2021年8月 中国建材科技 第30卷　第4期　 浅析缓凝剂对建筑石膏基本性能影响 摘要：通过在建筑石膏中应用不同类型的缓凝剂进行试验，探讨了缓凝剂对建筑石膏基本性能的影响。研究表明， 缓凝剂在掺量较低的条件下可较大幅度延缓建筑石膏凝结时间，同一种缓凝剂随掺量增加其凝结时间延长。试验 发现，不同缓凝剂对各种建筑石膏的适应性差别较大。同时，适量的缓凝剂对建筑石膏流动性能有一定改善作用。 过量的缓凝剂会损失石膏基材硬化体力学强度，对于大多数的石膏缓凝剂其适宜掺量应控制在0.1% 以内。 关键词：脱硫石膏；缓凝剂；凝结时间；力学强度 Abstract: The effects of different plaster retarders on gypsum are studied in this paper. The performance evaluation of these retarders is carried out through comparing the setting time, strength and slump flow of desulfurized gypsum. The results show that the retarder can immensely prolong the initial setting time and final setting time of gypsum while its effects are remarkable and its extension range is expanded with the increasing of dosage. The composite efficient modification retarders have good performance on promoting the slump flow of the gypsum slurry at a certain dosage. Too much retarder can decrease the mechanical properties of gypsum base hardening body. For most gypsum retarders, the suitable dosage should be controlled within 0.1%. Keywords: desulfurized gypsum; retarder; setting time; strength 中图分类号：TQ177.3　文献标志码：A　文章编号：1003-8965（2021）04-0045-03 烟气脱硫石膏作为燃煤电厂烟气脱硫后的工业副产废 等基本性能差别较大[8] 。石膏 1 的标准稠度用水量较小， 弃物经干燥、煅烧、研磨等工艺，可制备成性能良好的建筑 为 0.56 ；而石膏5 的标准稠度用水量为0.82。石膏 1、3 和 4 石膏。石膏具有轻质、保温、隔热等优点。随着人们对环 的凝结时间相对较长，石膏 5 的凝结速率较快，初凝小于 保的重视及对资源循环利用的关注，烟气脱硫建筑石膏被 3min。在力学强度方面，石膏5 的力学强度值较低，抗折强 广泛应用于装饰行业[1] 。和天然石膏相比，烟气脱硫建筑 度为 3.7MPa ，抗压强度为8.38MPa ；石膏2 和石膏 3 的力学 石膏具有颗粒均匀、比表面积小、品位高等特点[2] 。但是， 强度值较大，抗折强度分别为 8.3MPa、8.1MPa ，抗压强度 由于建筑石膏料浆凝结硬化速率较快，限制了建筑石膏在 分别为 22.58MPa 、21.67MPa 。从表 1可以看出，建筑石膏 建筑行业的应用[3-5] 。为克服这一缺点，可向建筑石膏胶凝 2h力学强度跟绝干力学强度有相关性，因为建筑石膏 2h 内 材料中加入适量缓凝剂，通过外加剂改善石膏基材的可操