硅粉和高炉矿渣双掺超高强度 混凝土基本物性研究 Study on the Basic Physical Properties of Ultra-high Strength Concrete Mixed with Silicon Powder and Blast Furnace Slag 摘要： 硅粉细度大，活性高，添加硅粉的混凝土强度增加极大，但硅粉需水量极大。高炉矿渣需水量较小，前期强度较低，但后期强 度呈明显增加趋势，且有递减混凝土水化热的效果，若将这两种混合料同时添加，预期可形成互补，产生叠加效应。 Abstract: Silicon powder has high fineness and high activity. The strength of concrete added with silicon powder increases greatly, but silicon powder requires a great amount of water. The blast furnace slag requires less water, and the early strength is lower, but the strength in the later stage is obviously increasing, and it has the effect of decreasing the hydration heat of concrete. If these two mixtures are added at the same time, it is expected to form a complement and produce a superposition effect. 关键词： 硅粉；高炉矿渣；流动性；密实结构 Key words: silicon powder ；blast furnace slag ；fluidity ；dense structure 中图分类号： 文献标识码： 文章编号： TU528.04 A 1006-4311 （2020）16-0163-04 DOI:10.14018/j.cnki.cn13-1085/n.2020.16.071 0 引言 ②混凝土的长度变化。 随着建筑结构物寿命要求的提高，高强度混凝土的使 对混凝土试件进行初期水养（1 周、4 周）后，转入大气 用实例呈现出日趋增多的状况。类似硅粉、微硅粉、高炉矿 养护，从而以周为单位，探讨其收缩的长度变化。 渣、粉煤灰等能够胜任低水灰比并且具有极佳强度发展 ③绝热温度上升实验。 性、施工便利性的添加料得到大量的使用。但是，与此同时 制作尺寸为30×30×30cm 的混凝土试块，将其放置于 有实验报告指出添加硅粉后的高强度混凝土会产生大量 泡沫塑料中，监控混凝土内部及表面温度的变化，对混凝 水化热，从而引起较大的混凝土收缩。因此，考虑在混凝土 土水化发热状态形成参考。 中使用硅粉的同时可以尝试添加一些低发热型的掺和物， 1.1 使用材料 以避免水化热过高而影响施工质量。 本实验研究所使用的材料见表1。 本研究以改善低水灰比混凝土的施工性、递减水化热 1.2 混凝土配合比 等为目的，在混凝土拌合过程中同时添加硅粉以及高炉矿 混凝土配合比见表2 。以水胶比18%、22%、26%为基 渣，并对其进行标准水养，以及40℃水养（模拟夏季混凝 准，高炉矿渣添加量为0% 、30%、50% ，硅粉添加量为均为 土浇筑、预制混凝土部件的制作）后的压缩强度、干燥收 10%。例如：22SF-BS8G-