(9622)--陶粒粒径及级配对陶粒混凝土力学性能的影响.pdfVIP

陶粒粒径及级配对陶粒混凝土力学性能的影响 摘 要 采用商洛大量堆存的钒尾矿为主要原料，加入少量黏土、长石制备不同粒径的陶瓷颗粒，以该陶粒作为轻质骨料制备陶粒混凝土。 研究陶粒粒径及陶粒级配对陶粒混凝土抗压强度和抗折强度的影响，确定制备高性能陶粒混凝土的最优陶粒粒径及级配。结果表明：陶粒体积配 V V 比 10 mm) ∶ 15 mm)=1 ∶1 制备的陶粒混凝土力学性能最优，抗压强度为58.5 MPa，抗折强度达16.2 MPa。 ( ( 关键词 钒尾矿；陶粒混凝土；陶粒粒径；陶粒级配 TU528.2 A 1000-8098(2020)03-0037-03 中图分类号： 　文献标识码： 　文章编号： Effect of Ceramsite Size and Gradation on Mechanical Properties of Ceramsite Concrete * Zhao Wei Wang Zhiyu Zhou Chunsheng Bai Guoqing (Shaanxi Key Laboratory of Comprehensive Utilization of Tailings Resources, Shangluo University, Shangluo, Shaanxi 726000) Abstrat In this study, a large amount of vanadium tailings stored in Shangluo were used as the main raw materials, and a small amount of clay and feldspar were added to prepare ceramsites with different particle sizes. The ceramsites were used as lightweight aggregate to prepare ceramsite concretes. The effects of ceramsite size and gradation on compressive strength and flexural strength of ceramsite concretes were studied. The optimal ceramsite size and gradation for preparing high-performance ceramsite concrete were determined. The results show that the ceramsite concrete prepared with ceramsite volume ratio of 10 mm to 15 mm being 1 1 has the best mechanical properties. Compressive strength of the ceramsite concrete is ∶ 58.5 MPa and flexural strength reaches 16.2 MPa. Key words vanadium tailings; ceramsite concrete; ceramsite size; ceramsite gradation 陕西商洛尾矿堆存量较大，综合利用率较低。采 尾矿作为主要原料，加入黏土、长石为辅助原料，采用 [1] [2 3] [4] - 用尾矿制备免烧砖 、陶粒 、泡沫混凝土 、透水 高纯度SiC 作为发泡剂。经过前期试验探索得出制 [5] [6] 砖 、发泡陶瓷 等高附加值产品，是目前尾矿综合