发泡剂对体育器材用交联PVC泡沫泡孔结构的影响.pdfVIP

18 塑料助剂 2022年第1期 （总第151期） 发泡剂对体育器材用交联PVC泡沫泡孔结构的影响 郭鹏举 （西安培华学院 ，西安710125） 摘 要 ：为解决常规发泡工艺下PVC泡沫泡孔直径过大的问题 ，提出基于改性AC的PVC发泡工 艺 ，利用硬脂酸锌对AC进行改性处理获得mAC,以mAC为发泡剂制备PVC泡沫 。经实验分析发现， 发泡剂mAC能够显著降低PVC泡沫泡孔直径 ，使PVC泡沫更加适应小型手持式体育器材的加工制造。 关键词 ：聚氯乙烯 ；泡沫 ；发泡剂 ；泡孔结构 doi: 10.3969/j.issn.l 671-6294.2022.01.0004 Effect of Blowing Agents on the Cell Structure of PVC Foam for Sports Equipment Guo Pengju （Xian Peihua University, Xian 710125, China） Abstract： In order to solve the problem of too large 以 ell diameter of PVC foam in conventional foaming processes, we put forward a PVC foaming process based on the modified AC（mAC）. In this process, AC was modified by zinc stearate and mAC was obtained, and PVC foam was thus prepared with mAC as a blowing agent. The experimental analysis shows that the blowing agent mAC can significantly reduce the diameter of PVC foams and make the PVC foam more suitable for the manufacture of small hand-held sports equipment. Keywords： polyvinyl chloride; foam; blowing agent; cell structure 高分子发泡材料是体育用品生产加工领域的 二丙烯酯 ，江苏普乐司公司；甲基丙烯酸缩水甘 一种重要材料 ，具有比强度高 、缓冲性能优良、 油酯（GMA） ,南京荣安公司 ；苯酹（PA） 、马 质轻等方面的特点 ，可用于网球杆 、冲浪板等体 来酸肝 （MA） ,中国蓝星公司 ；苯乙烯 （St）, 育户外产品的加工与制造 。而聚氯乙烯 （PVC） 富田化工公司 ；偶氮二异丁睛（AIBN） ,山东沾 泡沫的泡孔结构很大程度上受发泡材料的影响， 祥化工 ；液化MDI （MDI-100） ,烟台万华集团； 因此有必要对使用不同发泡剂时的PVC泡沫的泡 聚氯乙烯糊树脂 （PVC） ,沈阳化工公司 ；硬脂 孔结构加以深入研究［ ，-3,o 酸锌（ZnSt2） ,山东宝利莱公司 ；环氧树脂（E51）, 无锡树脂厂 ；甲苯二异氧酸酯（TDI） ,日本三井。 1实验部分 1.2实验仪器 1.1实验材料 XL-04A型万能粉碎机 ，常州文达干燥机械 偶氮二甲酰胺 （AC） ,杭州海虹化工集团；