换热器波纹管的腐蚀失效原因.pdfVIP

换热器波纹管的腐蚀失效原因

摘要：某公司管壳式换热器，运行不到2个月就发生严重泄漏现象，波纹管多处出现孔洞和裂纹。现场截取泄漏

波纹管管段，采用形貌观察、化学成分分析、金相检验和能谱分析等分析了波纹管的合金成分、组织结构和腐蚀产物

特征，综合服役环境和材料特征两方面的信息，对泄漏原因进行了剖析和讨论。结果表明：波纹管发生泄漏起源于

管内壁，管材组织中夹杂物过多是造成波纹管的耐蚀性减弱，诱发点蚀，进而穿孔的主要原因。

关键词：波纹管；失效分析；夹杂物；穿孔；裂纹

CorrosionFailureReasonofBellowsofHeatExchanger

Abstract:Acertaincompanysshellandtubeheatexchangerexperiencedsevereleakagewithinlessthan2monthsof

operation,withmultipleholesandcracksappearinginthebellow.Thesectionoftheleakingbellowwasintercepted

onsite,andthealloycomposition,microstructure,andcorrosionproductcharacteristicsofthebellowwereanalyzed

usingmorphologyobservation,chemicalcompositionanalysis,metallographicexamination,andenergyspectrum

analysis.Basedonthecomprehensiveinformationoftheserviceenvironmentandmaterialcharacteristics,thecauseof

theleakagewasanalyzedanddiscussed.Theresultsindicatedthattheleakageofthebelloworiginatedfromtheinner

wallofthepipe,andtheexcessiveinclusioninthepipetissuewasthemainreasonfortheweakeningofthecorrosion

resistanceofthebellow,inducingpittingcorrosion,andultimatelyperforation.

Keywords:bellow;failureanalysis;inclusions;holes;crack

换热器中的换热管是实现热量交换与传递的重率，提升设备运行的安全性和经济性。

要部件。50%的换热器故障是由换热管腐蚀造成目前，有关换热器波纹管腐蚀失效的报道有很

的[1-3]。某管壳式换热器服役不到2个月就发生了多，不同的材料和环境体系会造成不同的失效原因。

严重的腐蚀泄漏。堵管是换热器传热管泄漏的唯一应力腐蚀是常见的损伤原因之一，操作环境中的

补救办法，但过高的堵管率将严重降低换热器的效CI-是诱发应力腐蚀的主要因素[4}，材料中Cr、Ti

率，使其难以满足生产工艺要求而整体作废，极大地元素含量过低也是应力腐蚀的诱因[5]。除应力腐蚀

增加了生产成本。为了查明泄漏原因，辅助支撑换外，对于不锈钢类管材，点蚀也是一种常见的腐蚀形

热器的维护工作，有必要对换热器管束的泄漏原因态[6-7。由于具有承压减震的特殊作用，波纹管常服

进行分析，以便有针对性地采取防护措施，降低事故役于有交变载荷的环境中，疲劳也是导致其失效的原

因之一[8-9]。由上可知，波纹管的损伤与材料本身和

收稿日期：2023-04-12服役环境密切相关，损伤机制和形式多种多样10-2]。