异步轧制及退火工艺对铜箔的尺度效应影响研究.docxVIP

摘要

为提高铜箔的综合性能，运用轧制与退火工艺，通过对其金相与微观检测，得到铜箔的晶粒尺寸与织构之间存在显著的尺度效应，即织构越强，晶粒越细，则其综合性能越好。铜箔织构强度主要与铜箔晶粒尺寸和变形温度有关，而变形温度又与异步轧制工艺、退火工艺等因素有关。铜箔的尺寸效应主要体现在厚度方向上。本文以铜箔为研究对象，研究不同工艺条件下铜箔的微观组织特征、织构和力学性能特征以及晶粒尺寸对其影响规律。

关键词：异步轧制；异速比；退火工艺；铜箔；尺度效应

Abstract

Inordertoimprovethecomprehensiveperformanceofcopperfoil,therollingandannealingprocess,throughitsmetallographicandmicroscopicdetection,itisobtainedthatthereisasignificantscaleeffectbetweenthegrainsizeandtextureofcopperfoil,thatis,thestrongerthetextureandthefinerthegrain,thebetteritscomprehensiveperformance.Thetexturestrengthofcopperfoilismainlyrelatedtothegrainsizeanddeformationtemperatureofcopperfoil,andthedeformationtemperatureisrelatedtotheasymmetricrollingprocess,annealingprocessandotherfactors.Thesizeeffectofcopperfoilismainlyreflectedinthethicknessdirection.Inthispaper,themicrostructurecharacteristics,textureandmechanicalpropertiesofcopperfoilunderdifferentprocessconditionsandtheinfluenceofgrainsizeoncopperfoilarestudied.

Keywords:Asymmetricrolling;Differentialspeedratio;Annealingprocess;Copperfoil;Scaleeffect

PAGE

PAGE3

目录

TOC\o1-3\h\u15012摘要 Ⅰ

15227Abstract Ⅱ

175721绪论 7

18691.1研究背景 7

249171.2铜箔与相关工艺手段的研究 7

306921.2.1异步轧制技术的优势与特点 8

261621.2.2退火工艺的特点与目的 9

259931.3国内外研究现状 9

102881.3.1国内研究现状 9

327401.3.2国外研究现状 11

135001.4研究目的及意义 12

208782实验材料与方法 13

152262.1实验材料 13

95342.1.1实验材料的前处理 13

305372.1.2实验材料的轧制 13

3412.1.3轧制试样的热处理 14

61662.2铜箔力学性能检测 14

217182.2.1抗拉强度性能测试 14

318672.2.2硬度测试 15

23162.3铜箔微观组织性能检测 15

167152.3.1断口形貌 15

13852.3.2TEM分析 15

77912.3.3EBSD分析 15

244253性能分析 17

9673.1力学性能的影响 17

323803.1.1拉伸力学性能的分析 17

158453.1.2硬度的分析 17

318073.2显微组织的演变 18

271073.2.1晶粒的影响 18

29623.2.3断口形貌的分析 20

308813.2.2织构的影响 21

177434结论 24

17704参考文献 25

28578致谢 28

1绪论

1.1研究背景

随着我国的微制造、微机电系