改性PVDF中空纤维膜抗污染性能研究

杨亮;魏俊富;赵孔银;张环;刘剑波

【摘要】HydrophilicmodifiedPVDFhollowfibermembraneispreparedby

graftingacrylicacid(AA)ontoitssurfacebyhighenergyelectron

beam.Thepurewaterfluxandpermeationofbovineserumalbumin(BSA)

solution,humicacid(HA)solution,andsaccharomycetessolutionare

consideredtobethemainparametersthattomeasuretheanti-fouling

propertyofmodifiedPVDFmembrane.Theresultsindicatethatthepure

waterfluxofPVDFmembraneimprovednearly1timesbyhydrophilic

modification.ComparedtooriginalPVDFmembrane,thereductionratesof

permeationfluxofmodifiedPVDFmembraneforHAsolutionand

saccharomycetessolutiondecrease58％and37％,respectively.The

reductionrateofpermeationfluxofmodifiedPVDFmembraneforBSA

solutiondecreases35％comparedwiththeoriginalmembraneinalkaline

condition.%通过高能电子束辐照接枝丙烯酸制备了亲水改性PVDF中空纤维膜,

根据纯水通量和对牛血清白蛋白溶液、腐植酸溶液、酵母菌溶液的渗透性能研究

PVDF膜表面亲水改性对抗污染的影响.结果表明:辐照接枝改性使PVDF中空纤维

膜的纯水通量提高了1倍;改性膜对腐植酸溶液和酵母菌溶液的渗透通量下降率较

原膜分别降低58％和37％;碱性条件下,改性膜对牛血清白蛋白溶液的渗透通量下

降率较原膜降低35％.

【期刊名称】《天津工业大学学报》

【年(卷),期】2013(032)004

【总页数】5页(P10-13,42)

【关键词】亲水改性;PVDF中空纤维膜;膜污染;酵母菌;腐植酸

【作者】杨亮;魏俊富;赵孔银;张环;刘剑波

【作者单位】天津工业大学中空纤维膜材料与膜过程省部共建国家重点实验室培育

基地,天津300387;天津工业大学环境与化学工程学院,天津300387;天津工业大学

中空纤维膜材料与膜过程省部共建国家重点实验室培育基地,天津300387;天津工

业大学环境与化学工程学院,天津300387;天津工业大学中空纤维膜材料与膜过程

省部共建国家重点实验室培育基地,天津300387;天津工业大学材料科学与工程学

院,天津300387;天津工业大学中空纤维膜材料与膜过程省部共建国家重点实验室

培育基地,天津300387;天津工业大学环境与化学工程学院,天津300387;天津工业

大学环境与化学工程学院,天津300387

【正文语种】中文

【中图分类】TS102.528.1

PVDF是一种性能优良的高分子材料，其突出的化学稳定性、耐辐射特性、抗污染

性和耐热性更使其在膜分离领域大显身手，其中PVDF微滤膜和超滤膜已成功地

应用于化工、电子、纺织、食品、生化等领域[1-2].但PVDF树脂表面能极低，有

极强的憎水性，易产生吸附污染，使膜通量下降，降低了膜的使用寿命[3].膜的亲

水改性对抗污染十分重要[4-6]，因此改善PVDF分离膜的亲水性，提高膜的抗吸

附污染能力和降低膜运行中的动力消耗成为当前分离膜研究的热点[7].本文以

PVDF中空纤维超滤膜为基膜，通过高能电子束引发接枝聚合丙烯酸[8-9]，得到

改性PVDF中空纤维膜，然后对其抗污染性能进行测试分析.

1实验部分

1.1实验材料与仪器

所用原材料包括:甘油，分析纯，天津市医药公司产品；无水乙醇，分析纯，天津

市江天化工