STD 1014316-issue4-200401-金属材料维氏硬度检测方法-chs.pdfVIP

STD1014316-2004-01

Vickershardnesstest

共8页第1页

维氏硬度测试沃尔沃标准-其他

NOTFORNEWDESIGNASOF2004-01-01

Thisstandardisvalidwhenthereisareferencetoit.”Notfornewdesign”isonlyanindicationtoourdesign

departments.

不适用于2004-01-01的新设计

该标准在有参考时有效。“不是新设计”只是我们设计部门的一个指示。

Orientering

Thisissuediffersfromissue3inthatthestandardnolongerappliestonewdesign.

Fornewdesign,standardsSTD323-0003(VolvoGroup)andVCS1014,3169(VolvoCarCorporation)shallbeused.

ThisstandardcoversVickershardnesstestsofmetallicmaterials-VickersHV0,2toHV5andVickersHV5toHV

100(testforce1,961-(49,03)Nand49,03–980,7N).

WhentestingaccordingtotheVickersmethod,loadscorrespondingtotherangeHV5toHV100areused,for

examplewithinproductionandprocesscontrol,whileHV0,2toHV5areusedforspecificapplicationsrequiringa

speciallaboratorytechnique.Ingeneral,decreasingtestforceincreasesthescatterofresultsofmeasurements.

ThestandardagreeswithSS112516,issue6,andwithSS112517,issue2aswellaswithISO6507/1andISO

6507/2.

方向

此问题与问题3的不同之处在于该标准不再适用于新设计。

对于新设计，应使用标准STD323-0003（沃尔沃集团）和VCS1014,3169（沃尔沃汽车公司）。

该标准涵盖了金属材料的维氏硬度试验-维氏HV0,2至HV5和维氏HV5至HV100（试验力1,961-（49,03）N

和49,03-980,7N）。

当根据维氏方法测试时，使用对应于HV5至HV100范围的负载，例如在生产和过程控制中，而HV0,2至HV5用

于需要特殊实验室技术的特定应用。通常，降低测试力会增加测量结果的分散。

该标准与SS112516，第6期和SS112517，第2期以及ISO6507/1和ISO6507/2一致。

更改标记更改文件号更改内容