焊后消应力工艺对TC4焊接接头弯曲性能的影响.pdfVIP

《热加工工艺》20217月第50卷第13期

焊后消应力工艺对TC4焊接接头弯曲性能的影响

陈高澎，徐家磊，罗皓，徐希军，刘希林

(洛阳船舶材料研究所，河南洛阳471000)

摘要：选取了五种不同的消应力工艺对TC4焊接接头进行了焊后处理。结果表明：超声冲击、风铲冲击以及

540°C热处理使焊接接头处组织由马氏体转变成部分针状a,能够提高焊缝的弯曲性能；振动时效对于焊缝的弯曲性能

几乎无影响；65(TC热处理后焊缝组织更加粗大，降低了焊缝的弯曲性能。

关键词：TC4焊接接头；消应力；弯曲性能

DOI:10.14158/j.cnki.1001-3814.

中图分类号：TG441.8文献标识码：A文章编号=1001-3814(2021)13-0155-04

EffectofPost-weldStressReliefProcessonBendingProperty

ofTC4WeldedJoints

CHENGaopeng,XUJiale,LUOHao,XUXijun,LlUXilin

(LuoyangShipMaterialResearchInstitute,Luoyang471000,China)

Abstract：Fivedifferentstressreliefprocesseswereselectedforpost-weldtreatmentofTC4weldedjoints.Theresults

showthatultrasonicimpact,airchipperimpactand540°Cheattreatmentmakethestructureoftheweldedjointtransform

frommartensiteintoapartofneedle-likea,whichcanimprovethebendingperformanceoftheweld.Vibrationaginghas

almostnoeffectonthebendingperformanceoftheweld.Afterthe650°Cheattreatment,theweldstructureiscoarser,which

reducesthebendingperformanceoftheweld.

KeywordsTC4weldedjoint;stressrelief;bendingproperty：

钛合金具有高强度、低密度，抗蚀性能、耐高温、对TC4合金对接接头实施不同的焊后消应力工艺

焊接性能和韧性较好等众多优点，在航空、航天、海处理,分析研究其弯曲性能的影响因素。

洋、电力、化工、汽车制造及国防工业中得到广泛应

1工艺试验

用。其中，T-6A1-4V(TC4)合金作为一种典型ct+(3两

相钛合金，在深潜器耐压部件、飞