热轧H型钢麻面缺陷分析与改进.pdfVIP

2023年 6月河南冶金Jun.    2023

第31卷    第3期HENAN METALLURGYVol.31    No.3

热轧H型钢麻面缺陷分析与改进

肖克勇张丽娜石雷澎奎华锋李静

（马鞍山钢铁股份有限公司）

摘要   针对热轧H型钢出现的麻面问题，通过观察缺陷的宏观和微观形貌，分析麻面缺陷形成的原因为轧制过

程中氧化铁皮未及时去除、压入产品表面，轧制压缩比小、晶粒未充分细化产生。因此提出了采用优化加热工艺、

修改开坯和万能轧制规程、增加除鳞装置和成分设计等方法，有效控制热轧H型钢麻面缺陷，提高了产品表面

质量和客户满意度。

关键词    H型钢   麻面缺陷   二次氧化铁皮   轧制规程   成分设计

ANALYSISANDIMPROVEMENTOFHOTROLLEDH-SHAPEDSTEELPITTED

SURFACEDEFECTS

Xiao Kayong    Zhang Lina    Shi Lei    Peng Kui    Hua Feng    Li Jing

(Maanshan Iron  Steel Co., LTD.)

ABSTRACT   In view of the problem of pitted surface of hot-rolled H-shaped steel, by observing the macroscopic and 

microscopic morphology of the defects, it was analyzed that the causes of pitted surface defects were not timely removed from 

the pressed product surface during rolling, the rolling compression ratio was small, and the grain was not sufficiently refined. 

Therefore, the methods of optimizing heating process, modifying preforming and universal rolling procedures, adding phos-

phorus removal device and composition design are put forward to effectively control the surface defects of hot-rolled H-shaped 

steel, improve product surface quality and customer satisfaction.

KEYWORDS    H-shaped steel     Pitted surface defect     Secondary oxide sheet     Rolling regulations     Composition design 

0前言侧中间区域，如图1（阴影部分）所示。笔者针

H型钢因其具有抗弯能力强、价格便宜和结对马钢大H型钢产线生产的低合金Q355B级桩

构重量轻等优点，已快速应用到国民经济的各型400×408×21×21规格H型钢出现的腹板和翼

个领域[1-3]。随着市场对H型钢需求量的不断增缘外侧麻面，分析缺陷产生原因，结合生产工艺，

加，不仅对型钢的内在性能和尺寸公差提出严格