上海交大铜铝焊接方法1-s2.0-S0921509313007399-main.pdfVIP

MaterialsScienceEngineeringA583(2013)177–181

ContentslistsavailableatSciVerseScienceDirect

MaterialsScienceEngineeringA

journalhomepage:/locate/msea

Influenceofreductionratioontheinterfacemicrostructure

andmechanicalpropertiesofroll-bondedAl/Cusheets

K.S.Leea,n,S.E.Leea,H.K.Sungb,D.H.Leeb,J.S.Kimb,Y.W.Changb,S.Leeb,Y.N.Kwona

aKoreaInstituteofMaterialsScience,LightMetalDivision,MaterialsDeformationDepartment,797Changwondaero,Changwon,Gyeongnam642-831,

SouthKorea

bPOSTECH,DepartmentofMaterialsScienceandEngineering,Pohang790-784,SouthKorea

articleinfoabstract

Articlehistory:Two-plyAl/Cusheetswerepreparedviarollbondingwithdifferentreductionratios.Al/Cusheets

Received12May2013fabricatedbelow50%ofreductionratioexhibitedrelativelyequiaxedgrainswithoutinterfacereaction,

Receivedinrevisedformwhichresultedinweakjoint-bondingstrength.However,bothstrongmetallurgicalbondingatinterface

21June2013andfine,elongatedgrainsfromconstituentalloysadjacenttotheinterfaceweresuccessfullyintroduced

Accepted25June2013

underthereductionratioof65%,leadingtoastronglyenhancedbondingstrengthof17.1N/mmtogether

Availableonline8July2013

withanincreasedelongationuptofractureby28%.