转炉炉后渣洗脱硫试验研究.pdfVIP

转炉炉后渣洗脱硫试验研究 转炉炉后渣洗脱硫试验研究 赵彦华* 胡志刚 孙玉虎 李任春 盖领军 (邯郸钢铁集团公司) 摘 要 在转炉－LF －CSP 流程中，LF 精炼时间紧张和钢水增碳增硅现象常成为限制性环节。本文通过试验研究 了转炉渣洗脱硫的效果及其影响因素。结果表明：(1)渣洗脱硫主要发生在转炉渣进入钢包以前的几分钟时间内，预 熔渣的物化性能，诸如熔点、熔速、与钢水的润湿性和硫容量对渣洗脱硫率起决定作用；(2)渣洗脱硫剂的 CaO 含 量对渣洗脱硫效果影响很大；(3)转炉渣洗脱硫后，可缩短LF 精炼时间和减轻冷轧低碳钢的增碳和增硅现象。 关键词 预熔渣 LF 精炼 脱硫 Premelted Slag Infiltration Desulphurization Experiment During Converter Tapping Zhao Yanhua Hu Zhigang Sun yuhu Li renchun Gai lingjun (Handan Iron Steel Group Corp., Ltd.) Abstract It is limiting factor that the refining time of LF is long and the pickup of carbon and silicon in the converter —LF—CSP process. In this paper the desulphurizing efficiency and its influencing factors have been studied. It is indicated that: （1）slag Infiltration Desulphurization takes place in the first few minutes when converter slag is put in ladle, the parameters of premelted slag such as melting point, melting speed, wettability and sulfur capability play an decisive role; （2 ） the content CaO of premelted slag plays an important role in the desulphur effect, （3 ） it can efficiently reduce the pickup of carbon and silicon and LF refining time for cold rolled low carbon steel. Key words premelted slag ，LF refining ，desulphurization 1 引言 CSP 连铸连轧工艺具有节能、投资省、生产周期短、生产率高和成本低等优点，在全世界范围内迅速发 展 [1] 。由于CSP 工艺对钢水的硫含量要求较高，一般都采用LF 精炼工艺。LF 精炼效率高，脱硫效果好，升 温灵活，在CSP 生产线发挥了重要作用。但随着产量的提高，生产节奏不断加快，以及由于品种结构的调整， LF 的缺点也逐步暴露出来，主要表现在：(1) 由于脱硫任务重，精炼时间长，超过了转炉冶炼周期和CSP 铸机 浇钢时间，反而成为提高生产节奏的瓶颈制约因素，限制了连浇炉数的提高；(2)冶炼低碳钢时，特别是冶 冷轧低碳钢时，LF 炉在脱硫的同时，增硅、增碳的现象较严重，影响了产品的最终性能和合格率。 转炉炉后采用预熔渣渣洗脱硫工艺，操作方便，成本低，可有效地利用转炉出钢和钢包调运时间提前进 行渣系调整、提前化渣和预脱硫，可有效地缩短精炼时间[2,3]、提高精炼效率和CSP 连浇