金属氧化物涂层钛阳极的制备方法.pdfVIP

金属氧化物涂层钛阳极的制备方法/刘军梅等 ·38 · 金属氧化物涂层钛阳极的制备方法 刘军梅，郭振英，王海林 （中国钢研科技集团公司，北京 100081 ） 摘要 综述了不溶性阳极的发展状况，介绍了目前广泛应用的不溶性钛阳极——金属氧化物涂层钛阳极的制备方法， 包括热分解、溶胶-凝胶、磁控溅射和电沉积等方法，指出了每种制备方法的特点及应用范围，并展望了金属氧化物涂层钛 阳极的发展方向。 关键词 不溶性钛阳极 金属氧化物涂层 热分解法 溶胶-凝胶法 磁控溅射法 电沉积法 中图分类号：TB321 文献标识码：A The Preparation Method of Titanium Anode Coated with Metal Oxide LIU Junmei, GUO Zhenying, WANG Hailin (China Iron Steel Research Institute Group, Beijin g 100081) Abstract The development status of insoluble anode is reviewed. The preparation methods of the widely used insoluble titanium anode －titanium anode coated with metal oxide are introduced, including pyrolysis, sol-gel, magnetron sputtering and electrodeposition. The characteristics and applied range of each method are presented. Finally, the development trends of titanium anode coated with metal oxide are prospected. Key words insoluble titanium anode, metal oxide coating, pyrolysis method, sol-gel method, magnetron sputtering method, electrodeposition method 氧化物涂层电极大多采用金属钛作为电极基体，即金属氧化 0 引言 物涂层钛阳极。 阳极是电化学反应过程中提供电子、参与表面电化学氧 [1] 1 金属氧化物涂层钛阳极的制备方法 化反应的重要场所 。在电化学工业中，耐腐蚀阳极材料的 选择和制备一直是电化学工业的难题之一。近年来，不溶性 金属氧化物涂层钛阳极由基体金属钛和表面活性层组 阳极因具有尺寸稳定、不需要成膜、易维护、无潜在问题等 成[12] 。在制作之前，电极表面要进行预处理，目的是增强 优点[2—4] ，已经受到业内的广泛重视，并逐步应用于工程实 基体与金属氧化物涂层的结合力，从而改善导电性、延长使 [5] 践中 。 用寿命，同时也为涂层的制备做好准备。 不溶性阳极材料分为传统电极材料和新型不溶性阳极 目前，金属氧化物涂层钛阳极的制备方法很多[6,8,9,11] 。 [6]