不同粉磨方式矿渣粉对矿渣水泥流变性的影响.pdfVIP

不同粉磨方式矿渣粉对矿渣水泥流变性的影响/周胜波等 ·39 · 不同粉磨方式矿渣粉对矿渣水泥流变性的影响* 周胜波，侯新凯，刘 辉 （西安建筑科技大学材料科学与工程学院，西安 710055） 摘要 用激光粒度分析仪（LPS）研究了球磨和立磨粉磨的矿渣粉的粒度分布，用旋转粘度计对矿渣水泥的流变性能进 行了测量。发现：球磨机所加工的矿渣粉比立磨加工的矿粉颗粒尺寸分布宽、细颗粒含量高；矿渣粉比表面积相近时，矿渣 掺量在小于30%和大于40%时由球磨矿渣粉制成的矿渣水泥比立磨矿渣水泥的屈服应力和粘度小，而掺量在30%～40%之间时 球磨矿渣水泥的粘度和屈服应力较立磨的稍大。此外，对矿渣粉颗粒群与水泥流变性之间进行了灰色关联分析，发现小于 10μm的矿渣颗粒增加了水泥浆的屈服应力和粘度，而大于10μm矿渣颗粒却削弱了水泥浆的屈服应力和粘度。 关键词 立磨 球磨 矿渣粉 颗粒群特征 流变性能 The Effect of Blast Furnace Slag Power by Different Grinding Methods on Cement Rheology ZHOU Shengbo, HOU Xinkai, LI Hui (College of Material Science Engineering, Xi，an University of Architecture Technology, Xi，an 710055) Abstract The particle size distribution of blast furnace slag power ground by ball mill and LM was analyzed by means of LPS. And the rheology was measured by NXS .The results showed that the particle size distribution made by ball mill was wider and higher fine particle than LM; The slag cement shear stress and viscosity of ball mill was less than LM under the same specific surface area when the cement was substituted by slag less than 30% and more than 40%. And contrarily ball mill’s was bigger than LM’s when the cement was substituted by 30%~40% slag. The relationship between cement particle size distribution and the cement rheology was researched by grey correlation analysis method. The conclusion showed that the slag particle less than10µm increased the cement shear stress and viscosity and the slag particle more than10µm decrease the cement shear stress and viscosity. Key words ball mill ，LM ，blast furnace slag power ，particle size distribution ，rheology 水泥浆与水泥混凝土混合物的工艺特性，特别是通常 所称的工作性或和易性，是从事混凝土施工和水泥制品工艺 的粒度分布，同时用旋转粘度计测量矿渣水泥