纳米TiO2粉体的制备与性能表征.pdfVIP

·54 · 材料导报网刊 2006 年 3 月第 1 期 * 纳米 TiO 粉体的制备与性能表征 2 朱国平，周康根，郭朝辉 （中南大学冶金科学与工程学院环境工程系，长沙 410083） 摘要 以硫酸法生产钛白粉的中间产物偏钛酸为原料，利用盐酸溶解-氨水中和沉淀法，成功地制备了纳米锐钛矿型 TiO ，并采用热重分析、X 射线衍射、透射电镜等技术研究了纳米粉体材料的晶型结构和形貌特征。实验结果表明：所制的 2 前驱体水合TiO 粉体本身已具锐钛矿型，经600℃煅烧后粉体结晶性较好仍为锐钛矿型，平均颗粒粒径大小为20nm。 2 关键词 二氧化钛 纳米粉体 前驱体 Preparation and Characterization of Nano-sized TiO Powder 2 ZHU Guoping ，ZHOU Kanggen ，GUO Zhaohui (Department of Environmental Engineering, School of Metallurgical Science and Engineering, Central South University, Changsha 410083) Abstract Nano-sized anatase titanium dioxide was prepared by using hydrochloric acid diffluence and ammonia deposition method. This technics used the middle product, titanic acid as raw material, which come from the manufacture of titanium white. The powder was characterized by the measurement of TEM, TG-DTA, and XRD. The results showed that the crystal structure of hydration titanium dioxide was anatase, After 600 ℃ calcined the crystal structure also was anatase, and the average particle size was about 20nm. Keywords titanium dioxide ，nano-sized powder ，precursor 0 前言 TiOCl2 +3H 2 O → Ti(OH )4 (胶体) +2HCl 纳米 TiO2 由于细微的尺寸颗粒﹑较大的比表面积和 将正钛酸胶体溶液放入低速离心机中（调节速度，使胶 高效的光催化性能，使其在很多方面表现出独特的性能， 体与固体杂质分离），除去固体杂质，加入氨水调pH 至 7 左 成为性能极佳的光催化剂而在许多行业中得到了广泛的应 3+