应用Taguchi方法消除产品表面熔接痕的工艺研究.pdfVIP

研究与检测· Research and Test echnology of Eliminating Weldline on Products TSurface Using Taguchi Methods 应用Taguchi方法消除产 品表面熔接痕的工艺研究 摘 要：为提高注塑产品表面质量，消除产品表面熔接痕，本文利用Taguchi方法设计了L9实验矩阵， 分析了熔体温度、模具温度、注射压力、保压时间等工艺因素对ABS制品表面熔接痕长度的影响，预测了最佳 工艺参数，并在验证实验中消除了产品表面熔接痕，对注塑生产具有一定的指导意义。 关键词：注塑成型 熔接痕 工艺优化 Taguchi法 Abstract: In order to improve the surface quality of injection molded products, eliminate weld line on the products surface, an L9 experimental matrix is designed using Taguchi method to analyse the technology effects. The infl uence of melt temperature 、mould temperature 、injection pressure and packing time on the weld line length of ABS products surface is investigated. The optimal process parameter is predicted, and the weld line of the products surface is eliminated during the evaluation experiment. The results may provide some references for injection molding technology. Key words: injection molding weld line process optimum Taguchi method 文/丁 磊 伍晓宇 李伟荣 梁 雄 编者按：随着生活水平的提高，人们对塑料制品质量提出更高的要求，高光无接痕就是其 一，为此 业者开始了许多的试验去消除接痕。作者利用Taguchi方法设计了L9实验矩阵就是其中一种尝试。 着市场对高光无痕注塑产 略，但对塑件的表面质量影响较大[2]。 实验部分 品需求的增大，熔接痕的 目前，国内外多数关于消除熔接 随 消除再次成为注塑行业关 痕的工艺研究，主要是通过测量与分析 材料及设备 注的热点问题。熔接痕是指在制品成型 含有熔接痕的注塑试件的拉伸强度，来 ABS：奇美塑胶原料（东莞）有限 过程中, 两股以上料流前锋熔体汇合时， 确定各种工艺参数对熔接痕的影响程度 公司； 因前锋面上熔体温度下降，在熔体汇合 [3]。本文为研究熔接痕给注塑产品表面 注塑机：SP108A型，仁兴机械（深 处的制品表面上形成的接缝痕迹，常见 质量带来的影响，直接以熔接痕长度为 圳）有限公司； 的熔接痕种类有热接痕、冷接痕以及由 指标进行分析，选用丙烯腈-丁二烯-苯 模温控制设备：课题组自行开 于充模时熔体前沿的“喷泉”式流动或 乙烯共聚物(ABS)，以车载蓝牙外壳为 发的模具温控系统，主要由温度快 壁厚不均引起的熔接痕[1]。对于无定形 例，采用Taguchi实验设计理论，运用 速响