DBSA 掺杂的核-壳结构聚苯胺的合成与应用 王雅珍 贾宏葛 王峰 徐胜鹏 （齐齐哈尔大学化学与化工学院齐齐哈尔 161006） 摘 要 采用乳液聚合方法，利用PP 的二甲苯溶液为种子合成了核-壳结构的聚苯胺。探讨了 PP 的二甲苯溶液、十二烷基苯磺酸钠（乳化剂和掺杂剂）、过硫酸铵用量及pH 值对核-壳结 构聚苯胺的物化性质的影响。利用FTIR，DSC 高倍显微镜等手段对聚苯胺的分子结构，热稳 定性及与PP 共混的界面进行了测试分析。聚苯胺与PP 进行共混，制成了导电性较高，溶解 性和熔融性较好的抗静电共混材料。 关键词：聚苯胺 核-壳结构 掺杂 抗静电 Synthesis and Application of the Core-shell Structure’s Polyaniline doped by DBSA Wang-yazhen,Jia-hongge， Wang-feng;Xv-shengpeng. (Chemistry and Chemical Engineer College of qiqihar University,qiqihar 161006) Abstract The core-shell structure’s Polyaniline whose core is PP was synthesized by the emulsion polymerization,. The influence of the PP-xylene, dodecylbenzenesulfonic acid (DBSA), ammomum persunate (APS) and the pH have been investigated. By means of DSC, FTIR and microscope, physical property and chemical property of polyaniline was measured. Blend material of polyaniline and PP possesseing, antistaticity, dissolvability and fusibility was prepared. Key words: polyaniline; core-shell structure; doping; antistatic. 聚苯胺以其可获得的电学性能和环境稳定性从众多导电聚合物中脱颖而出，成为直至今 日学术界研究的热点[1-3]。近年来，聚苯胺的纳米材料成为科研人员关注的焦点，关于导电聚 [4] 苯胺纳米纤维、纳米粒子等纳米材料的报道日益增多 。 导电聚苯胺是苯胺分子1,4-偶联等轴反应的产物，这个偶联反应在pH=0～1 的酸性介质 中占优势，若反应体系 pH 值下降，就会生成越来越多的不导电的枝状副产物。Green 和 [5] Woodheead 用八聚体的形式形象地说明了聚苯胺的五种氧化态。虽然研究人员已经通过各种 方法合成了导电聚苯胺，但聚苯胺的合成机理却至今没有一个统一的解释。由于聚苯胺的难 溶难熔性导致其加工困难，这就注定聚苯胺要与其它加工性好的材料复合以制得综合性能优 良的导电材料。如何将聚苯胺与其它材料复合成导电材料是近年来科研人员研究的一个重要 课题。目前比较普遍的做法有溶液共混法、机械熔融共混法、乳液共混法和现场吸附聚合法 几种。闾兴圣等[6]对这几种方法进行了比较全面的介绍。 本实验所采用的PP 二甲苯溶液掺杂的聚苯胺乳液聚合方法，则是将PP 二甲苯溶液在乳 液环境中先形成均匀的分散相——核相，然后苯胺单体以核相为中心，在其表面逐步聚合， 最终形成壳相，即所谓的聚苯胺核—壳粒子聚合方式，取得了较好的溶解性和熔融性。 1 实验 1 1.1 实验药品