45钢电机轴断裂失效分析 顾宝兰，张雪涛，徐彤 （中国特种设备检测研究院 北京100013） 摘要：针对45钢断裂组织断口形貌测试分析。Fracture Failure Analysis of Electric motor shaft of 45 Steel GU Bao-lan, ZHANG Xue-Tao，Xu Tong (. china special equipment inspection and research institute, Beijing 100013 china) Abstract: The fracture failure reason of electric motor shaft was analyzed by means of examination of chemical composition，mechanical properties, micrography and fractography. The result indicate that there has stress concentration at the root of knuckle diameter of the shaft, where had small curvature radius and large machining roughness, the intensity of the shaft was not enough with the annealing treatment and the high content of MnS in the steel lead to the decrease of the mechanical properties result in the fatigue failure of the shaft at alternate loading. Keywords: 45steel; fatigue fracture; failure analysis 引言 某厂干燥机的电机轴，规格为Ф36mm，投入使用时间超过10年，使用过程中发生断裂，轴的材料为45钢，该电机轴在工作过程中主要承受交变弯曲应力和扭转应力的作用，为了找出电机轴断裂的原因，通过化学成分、力学性能、金相组织及断口分析等项目的测试分析，对失效的原因进行了分析。 1 理化检验 1.1 材料成分分析 在断裂轴上截取一组试样，采用光电直读光谱仪进行化学成分分析，分析结果见表1。对比测量值及标准要求要求，可以确定轴的材料化学成分满足JB /T 1271-2002《交、直流电机轴锻件技术条件》化学成分的要求。 表1 45钢化学成分分析结果 Table 1 The chemical composition of 45 steel (%) 化学元素 C Si Mn P S 实测值 0.46 0.24 0.62 0.017 0.018 JB /T 1271 规定值 0.42 ~0.50 0.17 ~0.37 0.50 ~0.80 ≤0.025 ≤0.025 1.2力学性能测试 距断裂面10mm距离处，切取3根轴向拉伸试样，2个V型缺口冲击试样及3个U型冲击试样，进行屈服强度（ReL），抗拉强度（Rm）及断后伸长率（A）以及冲击吸收功（AKu，AKv）的测量，并切取一段试样测量硬度值，测量结果见表2，结果显示，该材料力学性能满足JB /T 1271-2002的要求。 表 2 45钢力学性能测试结果 Table 2 The mechanical properties results of 45 steel 试样编号 下屈服强度ReL N/mm2 抗拉强度Rm N/mm2 断后伸长率A % 冲击吸收功 洛氏硬度 HRB Aku（J） Akv（J） 1#实测值 354 637 30.8 30 18 表面 87 2#实测值 357 639 27.6 26 20 3#实测值 356 639 24 28 / 心部 87 JB /T 1271-2002 标准值 ≥275 ≥540 ≥12 ≥24 / 1.3金相组织分析 对断裂轴横向及纵向分别取样进行金相组织分析，经过机械研磨及抛光后，采用4%硝酸酒精腐蚀，其表层及心部的组织均为碳钢正火或退火态的组织铁素体+珠光体。图1所示为横向金相组织形貌，可以看出，轴的心部组织的晶粒度大于轴表层组织，且心部组织铁素体呈网状分布。图2所示为纵向金相组织形貌，铁素体和珠光体组织均呈带状分布，且在铁素体基体上分布着大量的MnS带状夹杂物，最严重区域含量达3级，见图3。 a）心部组织b）表层组织 图1 横向金相组织形貌 Fig 1 the tran