连铸大方坯非金属夹杂物研究 杨 玉 庞兆夫 金纪勇 （鞍钢技术中心，鞍山 114009） 摘 要 我们通过定量金相法和化学电解法对连铸生产时不同浇注部位连铸坯内部非金属夹杂物的分布情况进行 了详细分析，结果表明：连铸时，首炉第一支连铸坯的夹杂物明显多于其它连铸坯；铸坯中的硫化物夹杂以硫化铁 为主；氧化物夹杂以二氧化硅为主；在连铸坯的内外弧1/4 处及左右宽度的1/4 处夹杂物分布最多。 关键词 连铸坯 非金属夹杂物 硫化物 氧化物 The Study of Nonmetallic Inclusions in Continuous Cast Bloom Yang Yu Pang Zhaofu Jin Jiyong （The Technical Center of Anshang Steel Company ，Anshan ，114009） Abstract we did the detailed analysis of the distribution of the inclusions in different parts of the continuous metal cast square billets. The results show that the first billets of the first stove apparently contains much more inclusions than others. The sulfide inclusion is mainly in the form of ferric sulfides; The oxides inclusion is mainly in the form of silicon dioxide; It is also found that the amount of inclusion at about ¼ of the inner and outer arc and ¼ lengths from left and right is much more than other places. Key words continuous metal cast billet，nonmetallic inclusions ，sulfide inclusion，oxides inclusion 1 引言 随着连续铸钢工艺的广泛应用和发展，人们对连铸坯质量要求越来越高。连铸坯表面缺陷一般可通过调 整操作条件得到改善，裂纹、中心偏析、气泡等内部缺陷可利用低倍酸侵检验及时发现并采取措施解决，而 细小的非金属夹杂物并不能用方便快捷的方法检验出来。本文就大方坯内非金属夹杂物种类及分布情况进行 了较详细的研究分析。 2 研究方法 连续浇铸时铸坯的浇注位置对夹杂物分布的影响很大，因此，我们选择浇次首炉首坯、首炉 4 支坯及 非首炉的一支铸坯取样进行研究，保护渣为生产上常用的碱性渣。 一般认为连铸坯表层柱状晶区杂质比较少，而铸坯的对角线处的柱状间界及内部等轴晶区是杂质等缺陷 易聚集的区域，这些区域应是我们研究的重点。通过观察重轨连铸坯的枝晶图，测量其表层柱状晶区范围及 对角线位置，确定了取样分析的范围为：内外弧侧50mm、左右宽度距两边部60mm 以内部分，一条对角线 上两角其余部分，与内外弧垂直的中心线上两边部。具体取样位置见分析结果图。 为方便对比分析，我们选用定量测量的方法来评估夹杂物的分布情况,包括金相法及电解法。 金相法：每块铸坯取48 个金相试样（具体取样位置见分析结果图），每个金相试样面积为30mm ×25mm 。 试样磨制抛光后在光学显微镜下观察，单个测试视场面积0.36mm ×0.24mm，随机连续测定10 个视场，计 算出单位面积内夹杂物个数。为分析方便，我们划定了数值范围，在取样图中以不同的颜色显示。同时找 整个试样测试视场内的最大夹杂物，测量其尺寸，以图标示。 杨玉，女，生于 1977 年 10 月 20 日，学士，工程师，电子邮箱：yangyu_girl@ *