Progress in Natural Science: Materials International 2012;22(5):426–432 Chinese Materials Research Society Progress in Natural Science: Materials International /locate/pnsmi ORIGINAL RESEARCH Effect of long term aging on microstructure and stress rupture properties of a nickel based single crystal superalloy n Zhenxue Shi , Jiarong Li, Shizhong Liu Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095, China Received 9 June 2012; accepted 26 July 2012 Available online 11 November 2012 KEYWORDS Abstract A nickel based single crystal superalloy with [001] orientation was prepared by the screw selecting method in the directionally solidified furnace. The long term aging (LTA) of the alloy after Single crystal superalloy; Long term aging (LTA); full heat treatment was performed at 1040 1C for 200–800 h. The microstructure and stress rupture Microstructure; properties at 980 1C/250 MPa and 1070 1C/140 MPa of the alloy long term aged (LTAed) for Stress rupture properties different time were investigated. The coarsening g0 phase and the broadening g matrix channel are observed in the samples LTAed at 1040 1C, but the g0 morphology is still in cubic shape after LTA for 800 h. No TCP phase precipitates after LTA for 400 h, while needle shaped and granular TCP phase forms in dendritic core of the alloy after LTA for 600 h. With increasing aging time