新型干拌砂浆稠化粉研究[J].docVIP

新型干拌砂浆稠化粉的研究 于利刚，黄宏伟，候兰辉，黄家琪 广东省建筑材料研究院，广东，广州 510160 摘要：砂浆添加剂是预拌砂浆的技术核心，本试验所研究的稠化粉是一种用于干拌砂浆的新型添加剂，具有保水增稠作用，掺入之后不仅能改善砂浆的和易性和保水性，还能明显提高砂浆的各项性能指标。对比其他市场销售的稠化材料，本试验研究的稠化粉具有更好的性价比。 关键词：稠化粉；干拌砂浆 Study on New thickening powder for dry-mixed mortar Yu Ligang, Huang Hongwei , Hou Lanhui, Huang Jiaqi GuangDong Building Material Research Institute Abstract: Mortar additives are one of the key technologies of ready-mixed mortar. In this paper, the thickening powder with water-retentive and plastic effect were prepared When it was added into the dry-mixed mortar, the workability and water retentivity of the mortar are improved, and other properties of the mortar are also remarkably increased. Compared to other marketing thickening powders, the thickening powder studied in this paper is highly cost-effective. Key words: thickening powder; dry-mixed mortar 1、前言 随着国家商务部、建设部等部门联合在我国部分城市限制禁止搅拌砂浆工作的开展，预拌砂浆作为一种新型建筑材料在全国得到了迅速的发展。可以预见，预拌砂浆，特别是普通干拌砂浆将成为继商品混凝土后的又一量大面广的建筑材料。 与传统砂浆配制技术相比，干拌砂浆的技术核心是砂浆添加剂。砂浆添加剂几乎决定了干拌砂浆的产品质量、使用性能，以及干拌砂浆的成本，也可以说，干拌砂浆是否具有市场竞争能力，其核心取决于砂浆添加剂的使用。目前，国内生产普通干拌砂浆的企业所使用的添加剂主要包括纤维素醚类、消化石灰粉类、以及以非石灰类无机材料为载体的保水增稠材料。其中，纤维素醚类使用效果较好，但是由于其价格高，加之在砂浆中掺量少，计量控制难度大，难以在混合搅拌时分散均匀，因此造成干拌砂浆成本高、生产质量控制难度大；消化石灰粉类外加剂则由于其对环境的污染以及质量难以控制而基本被限制或淘汰；保水增稠材料则由于其价格低、在生产中易于控制而越来越得到砂浆生产企业的重视，这种材料以非石灰类无机材料为载体，不易受潮，在配料时易于控制，在砂浆中可以有效改善砂浆的工作性能及保水性能。 然而，目前市场上出现的保水增稠材料从产品品种到质量品质上差异非常大，价格从几百元到几万元不等，加之没有相关标准，令生产企业无所适从。事实上，作为普通干拌砂浆，其主要特点是用量大、价格低，质量指标以满足保水性和施工性能为主，因此其添加剂应能够满足以下要求： 价格较低，不宜超出现拌砂浆太多，以使普通干拌砂浆能为市场接受； 掺量不宜过低，应该在2％以上，否则普通干拌砂浆生产的计量和混合设备很难满足要求，增加了生产成本； 干拌砂浆的稠度和保水性要好，能够满足施工要求，强度、抗渗性、粘结性能够达到标准要求即可。 本文以上述要求为试验目标，配制出成本较低，以高吸附性层状硅酸盐类无机材料为主体的有机－无机复合稠化粉，专用于普通干拌砂浆，不仅可以明显改善砂浆的和易性和保水性，还可以大幅降低水泥用量，有效提高砂浆的性价比。 2、原材料与试验方法 2.1 原材料 水泥采用广州石井水泥厂生产的42.5R普通硅酸盐水泥，河砂细度模数为2.3，粉煤灰为二级灰。 所配制的新型稠化粉以具有高吸附性的层状硅酸盐类无机材料和工业废渣为主要材料，选用无机盐改性剂和有机烷基盐改性剂进行复合改性，材料和改性成本约800元左右，试验代号为ZW，推荐掺量为砂浆总量的4％。 为进行对比，试验选择了在广东地区销售的部分稠化材料进行了比对研究，分别是： 稠化粉A：华东某地生产稠化材料，市价600元，推荐掺量4％； 稠化粉B: