摘要：传统的观点认为在焊缝及近缝区存在着残余压缩塑性应变，而近几年有学者提出焊缝不存在残余压缩塑性应变，只存在拉伸应力和应变，在焊后焊缝当中不可能存在残余压缩塑性变形，从而对消除残余应力的方法进行了重新论述，现根据这种新的观点及消除残余应力的若干问题，通过对接焊缝的数值模拟来验证这种新观点是否正确，并就消除残余应力应变问题针对一些矛盾的观点进行分析和讨论。 关键词：残余应力，应变，数值模拟 Analysis and Discussion About Forming Mechanism of Welding Residual Stress and Correlation Problem Yang Jiangguo Zhang Xueqiu Liu Xuesong Fang Hongyuan (State Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin, 150001) Abstract: Residual compressive plastic strain presents in the weld and heat affected zone from traditional views，but some scholars put forward that no residual compressive plastic strain lies in the weld, only tensile stress and strain, therefore no compressive plastic distortion is produced and think methods of removing the residual stress should be discussed renewedly. Basing on the new viewpoint and some problem of removing residual stress, numerical simulation of welding is adopted to analyse the inconsistent views. 0序言 1965年，前苏联尼古拉也夫Г﹒А院士分析了焊接应力应变发展过程，其原理见图１，在钢板中心区为压应力和压应变区，而板的两侧为拉应力和拉应变区。在大约200 ℃以上的区域产生压缩塑性变形，在600 ℃以上的区域，压缩塑性变形为α·T ，式中α为线膨胀系数，T 为温度［１］；此外，前苏联的H. O. 奥凯尔勃洛姆和C. A 库兹米诺夫也认为焊接加热过程中焊缝和近缝区的金属热膨胀应变受到周围较冷金属的拘束，从而产生压缩塑性应变。焊接冷却过程中该压缩塑性应变被拉 　 　 图1 　低碳钢板焊接纵向应力应变分布 Fig. 1 Longitudinal stress and strain distribution patterns 　 伸抵消一部分，但焊后仍残留部分压缩塑性应变，称为残余压缩塑性应变［２］［３］。并用来分析和预测焊接残余应力和变形。从而可以看出传统的观点，无论是尼古拉也夫Г﹒А院士还是H. O. 奥凯尔勃洛姆和C. A 库兹米诺夫，都认为焊缝存在压缩塑性变形。近几年，沈阳金属所的王者昌研究员提出了一种新的观点认为“对于焊缝金属来说，并不存在加热阶段。在冷却过程中除相变外，都受到拉伸，也就是说不存在压缩，更不会出现压缩塑性变形。”究竟是传统的残余压缩塑性应变理论正确还是王者昌研究员的观点正确，现以低碳钢对接焊缝的数值模拟来分析和验证焊缝的残余应力和残余压缩塑性应变的正确性。 1．对接焊缝的数值模拟 过去人们在研究焊接应力与应变方面大多采用解析法，但是由于该方法是基于平截面假设的前提下，并简化了诸多条件和因素，进行了多种假设后而进行的计算，掩盖了许多现象，伴随着计算机技术在焊接研究中的广泛应用，以数值模拟的方法来分析焊接应力应变及预测焊接变形已经成为了一种主要手段，虽然焊接数值模拟技术是从解析法发展起来的，但其可以定量地分析焊接行为的整个动态变化，能够近于准确地演示热弹塑性应力和应变非线性变化的复杂变化过程，由于数值模拟技术在近30年来取得的进展及在研究焊接问题上受到的认可，现在就采用数值模拟的方法来分析一下熔化焊焊缝及近缝区应力和应变情况。 传统的残余压缩塑性应变的观点一直假设是线热源对焊缝一起加热或认为焊缝本身作为待熔化金属的一部分，焊