Super304H+受热面管沿晶开裂研究.pdfVIP

Super304H 受热面管沿晶开裂研究 孙标 梁军 赵慧传 杜晋峰 神华国华（北京）电力研究院有限公司，北京，丰台，100069 Study on intergranular cracking of heating surface tube of Super304H Abstract: The intergranular cracking of heating 某电厂 6 号机组三级过热器的失效为出发 surface tube made of Super304H occurred during USC 点，研究分析 Super304H 的沿晶开裂的原因 unit’s construction was studied, the result which came 并提出解决措施，为电厂的安全运行提供实 form the metallographic analysis and intergranular 际指导。 corrosion for the failure components showed 1 锅炉受热面过热器 Super304H 管产 intergranular cracking of heating