原创力文档- 1、原创力文档（book118）网站文档一经付费（服务费），不意味着购买了该文档的版权，仅供个人/单位学习、研究之用，不得用于商业用途，未经授权，严禁复制、发行、汇编、翻译或者网络传播等，侵权必究。。
- 2、本站所有内容均由合作方或网友上传，本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺！文档内容仅供研究参考，付费前请自行鉴别。如您付费，意味着您自己接受本站规则且自行承担风险，本站不退款、不进行额外附加服务；查看《如何避免下载的几个坑》。如果您已付费下载过本站文档，您可以点击 这里二次下载。
- 3、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等，请点击“版权申诉”（推荐），也可以打举报电话：400-050-0827(电话支持时间：9:00-18:30)。
- 4、该文档为VIP文档，如果想要下载，成为VIP会员后，下载免费。
- 5、成为VIP后，下载本文档将扣除1次下载权益。下载后，不支持退款、换文档。如有疑问请联系我们。
- 6、成为VIP后，您将拥有八大权益，权益包括：VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
- 7、VIP文档为合作方或网友上传，每下载1次， 网站将根据用户上传文档的质量评分、类型等，对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档
查看更多
Plastic anisotropy and fracture behavior of AZ31 magnesium alloy
1 1 1, 2
LIU Pei , XIN Yun-chang , LIU Qing
1. College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China;
2. National Engineering Research Center for Magnesium Alloys, Chongqing University, Chongqing 400044, China;
Received 25 September 2010; accepted 20 December 2010
Abstract: The effects of texture and abnormal large grains on the plastic anisotropy and fracture behavior of hot-rolled AZ31
magnesium alloy were investigated. Uniaxial tensile deformation behaviors of samples with tensile axis tilting 0°, 15°, 30°, 45°, 60°,
75° and 90° to normal direction (ND) respectively were addressed. Tensile deformation anisotropy was observed for samples with
different angles to ND. The results show that the specimens with the angle from 0° to 30° exhibit relatively lower yielding strength
due to the {10 12} extension twinning. However, basal slip and prismatic slip are the dominant deformation modes for the
specimens with angles larger than 45°. Macro-fractures are parallel to the length direction of abnormal large grains in the specimens
with angles less than 60°, while those are serrated fracture edge for specimens with angles 75° and 90°.
Key words: AZ31 magnesium alloy; anisotropy; deformation mechanism; fracture
magnesium alloy, which will depend on the
1 Introduction understanding on plastic deformation mechanism of