子导电性的影响沈杭燕郭.pdfVIP

《化学通 》在 版 报 线预览 氯离子对介孔氧化铝质子导电性的影响 沈杭燕 郭冰 舒康颖 (中国计量学院理学院，杭州 310018) 摘要 掺杂氯盐使介孔氧化铝导电率提高近一个数量级，将掺杂的介孔氧化铝浸渍在水中 24h 后的导电率仍为纯 介孔氧化铝的 3~6 倍。红外光谱结果显示,氯掺杂改变了表面酸碱活性中心，导致质子更易在介孔氧化铝中发生迁移, 从而提高导电性。 关键词 质子导电性 介孔氧化铝 氯离子掺杂 Effect of Chloride on the Proton Conductivity of Mesoporous Alumina Shen Hangyan，Guo Bin，Shu Kangying (College of Science, China Jiliang University, Hangzhou 310018) Abstract The conductivity of mesoporous Al O was improved over one order by doping chloride, and the 2 3 conductivity of doped sample after immersion in water was still higher than that of pure Al2O3 3~6 times. IR results suggested that the hydrogen bonding between the hydroxyl and surface site became weak with doping chloride, which lead to the easy dissociation of the proton from the surface site and the increase of the conductivity. Keywords Proton conductivity, Mesoporous Al O , Doping, Chloride 2 3 质子交换膜燃料电池(PEMFC)是一种高效、对环境友好的发电装置。作为 PEMFC 的关键组件之一，质子 交换膜的性能和价格在很大程度上决定了电池的性能和成本。目前普遍使用的全氟磺酸膜 Nafion 由于其价格昂 贵，在高湿度下才具有高导电性且膜的阻隔性能较差等，使 PEMFC 的应用受到较大限制。因此，迫切需要开 发新的高性能低成本的电解质材料。 由于无机介孔导电体的其骨架具有良好的化学稳定性和热稳定性，具有Nafion 一样的孔道结构，在孔表面 可以置入大量羟基而吸附水，而且价格便宜，因此可能是一种优良的替代品。目前直接将无机多孔导电体作为 质子导电体的研究较少， Nogami 等[1,2]研究的五氧化磷搀杂的氧化硅其导电率在某些温度范围已超过了Nafion ， 但是这种材料不稳定，将它浸入水中，导电率降低了 3 个数量级。Anderson 等[3~5]上世纪 90 年代初研究了 γ-氧 化铝、氧化硅和氧化钛质子导电体，但导电性均比 Nafion 差。 笔者已研制出具有高质子导电性的系列介孔氧化铝材料，并且详细研究了导电率随材料孔径的变化规律 [6,7] 。本文报道了氯离子掺杂对介孔氧化铝导电性的影响，并分析了氯离子对介孔氧化铝导电性的影