手工电弧焊单双面焊接缺陷及防止措施.docVIP

长春汽车工业高等专科学校 继续教育学院 毕业论文 中文题目：手工电弧焊单双面焊接缺陷及防止措施 英文题目：SMAW welding defects in single-sided and Prevention 毕业专业：汽车制造与装调技术（汽车冲焊方向） 学生姓名： 王春月 准考证号： 291712101940 指导教师： 沙中玉 二零一三年九月 摘要 单面焊双面成形的焊接质量受到了焊接设备、焊材工艺流程、操作技术水平的限制造成质量差的原因，提出了相应的防止措施，对单面焊双面形单面焊双面成形焊接质量原因措施Forming side welding quality of welding by welding equipment, welding processes, operating technical limitations. This paper describes in detail welding power, welding current, welding speed, arc voltage, welding layers, rod-shaped type, electrode diameter and other technological factors on forming side welding technology welding quality and cause related defects. Detailed analysis of the forming side welding technology welding caused by poor quality caused a series of problems and the causes of poor quality, proposed the corresponding preventive measures to address side welding defects forming technology to make double-sided welding surface forming technology to further improve, promote them, and forming side welding job has a guiding role. Keywords: Side welding forming, welding, quality, reason, measures 目录 第一章 单面焊双面成形技术的概念 1 第二章 单面焊双面成形常见的焊接缺陷 2 2.1 尺寸上的缺陷 2 2.2 结构上的缺陷 2 2.3 性质上的缺陷 2 第三章 单面焊双面成形质量差引起的问题 3 3.1 增加消耗，降低结构的质量和使用寿命 3 3.2 焊接缺陷会给结构的安全生产带来威胁，引起安全事故 3 第四章 单面焊双面成形焊接质量差的原因分析 4 4.1 焊接电源自身因素引起的焊接质量差 4 4.2 工艺因素对单面焊双面成形焊接质量的影响 4 4.2.1 焊接电流 4 4.2.2 焊接速度 4 4.2.3 电弧电压 5 4.2.4 焊接层数选择不当 5 4.2.5 焊条类形及焊条直径的影响 5 4.3 操作因素 6 第五章 防止单面焊双面成形焊接产生焊接缺陷的措施 7 5.1 作好焊前准备 7 5.2 焊接操作 7 5.2.1 选择合适的工艺参数 7 5.2.2 焊工技术水平 8 结 论 9 参考文献 10 谢辞 11 第一章 单面焊双面成形技术的概念 单面焊双面成形技术是采用普通焊条，在不需要任何辅助措施条件下，只是坡口根部在进行组装定位焊时，应按焊接的不同操作手法留出不同的间隙，在坡口的正面进行焊接，就会在破口的正、背两面都能得到均匀整齐、成形良好，符合质量要求的焊缝。这种方法主要适用于板材对接接头、管状对接接头和骑座式管板接头。是锅炉、压力容器焊工应熟练掌握的操作技能。 （1）适用范围广,焊条直径小，可使用小焊接参数焊接，可以全位置焊接，而且更适应在某些重要焊接结构制造过程既要求焊透又无法在背部进行清根和重新焊接中使用。 （2）采用明弧焊接,明弧焊接熔池可见度好，便于观察，操作方便。 （3）焊后变形小成型均匀,由于电弧热量集中，熔池体积小，热影响区窄，焊缝塑性好，焊件焊后变形小焊缝外观成型光滑均匀，能得到