基于脉冲涡流的带保温层管壁腐蚀电磁检测系统_林俊明.pdfVIP

基于脉冲涡流的带保温层管壁腐蚀 电磁检测系统 林俊明 林发炳 林春景 （爱德森（厦门）电子有限公司，福建 厦门，361004） 摘要：介绍了用脉冲涡流的方法，可以隔着保温层和防腐层检测出试验材料的壁厚腐蚀和减 薄情况，阐述其基本原理、实测结果和发展现状。针对隔热层下钢管壁厚腐蚀减薄的 检测问题，根据电磁涡流无损检测原理，研制出了隔热层下管道壁厚脉冲涡流检测系 统。该系统可在役（不中断设备运行）检测隔热层厚度 100 mm 以上的钢管壁厚。 关键词：电磁检测；保温层；脉冲涡流；腐蚀 An electromagnetic system of pulsed eddy current for the corrosion inspection of tube walls with thermal insulation layers Lin Junming, Lin Fabing, Lin Chunjing (Eddysun (Xiamen) Electronic Co. Ltd., Xiamen, 361004) Abstract: The pulsed eddy current method has been introduced for the corrosion inspection and metal loss of pipe walls with thermal insulation layers or anticorrosion coating. The corresponding basic principles, experiment results and developments are presented. An electromagnetic system of pulsed eddy current for the corrosion inspection of tube walls with thermal insulation layers has been developed. This system can be applied for the in service thickness determination of pipe walls with about 100 mm thermal insulation layers Keywords: electromagnetic testing, thermal insulation layers, pulsed eddy current, corrosion 1 前言 各种管道的腐蚀缺陷检测是目前国际无损检测领域的研究热点，也是一项十分复杂的系 统工程，涉及众多前沿研究领域。长期以来，对保温层下管壁腐蚀状况的检测是电力石油、 化工和天然气行业中悬而未决的难题。目前，相关装置的检测对象都是曝露在外的管道，用 于检测覆盖有保温层和防腐层的管道则有困难。检测这类腐蚀要先去掉保温层，再用常规无 损检测技术进行检测，然后重敷保温层，有时还需要停止设备的运行，外包装的撤去和复原 费用昂贵而且耗时长。 2 管壁腐蚀检测技术的发展现状 2.1 管道的常规无损检测 目前，国内外管道常用的检测方法有磁粉检测、管道内电视摄像法、漏磁检测法、超声 波检测法、远场涡流检测法和射线检测法等。其中，使用较为广泛和成熟的方法是漏磁检测 法和超声波检测法[1]。 漏磁传感器检测圆周方向的裂缝裂纹、腐蚀沟槽等比较有效，具有较高的检测可靠性和 检测精度。但是，该技术不适合于检测形状复杂的试件，损伤的形状特征和检测的信号特征 不存在一一对应关系，损伤的量化理论有待进一步的研究。超声传感器对壁厚等径向变化敏 感，检测腐蚀坑等大面积损伤有效。 超声具有很强的穿透能力，可以测量管道内壁，外壁及壁内的损伤；探头可以采用不同 的大小，不同的发射频率及不同的布设角度，以探测更多种类的损伤，提高对损伤的检出率。 但是管道环境复杂多变，字损伤射频回波的解释比较困难，如何从损伤的超声回波中提取有 用的信息，一直是当今无损检测领域的研究热点。 2.2 管壁腐蚀的脉冲涡流检测 随着检测技术的进步，近年来根据超声波连续测厚和导波技术的远距离诊