刚性隔热材料的力学性能研究 孙陈诚 胡子君 王钦 鲁胜 张宏波 陈海坤 (先进功能复合材料技术国防科技重点实验室，航天材料及工艺研究所，100076，北京) 文 摘：采用纤维烧结法制备了刚性隔热材料，研究了材料密度、纤维 取向、测试温度、与气凝胶复合等因素对材料力学强度的影响规律。结果表 明：隔热材料力学强度随着密度的提高而增加；隔热材料平面方向拉伸＆压 缩强度均达到厚度方向的 4 倍以上；800℃和 1000℃下，材料的压缩强度保 持率分别达到 90％和 50％；与气凝胶复合后隔热材料在拉伸强度维持不变 的情况下，压缩强度增加 35％以上。 关键词：刚性隔热材料，力学性能 Mechanical Properties of Rigid Thermal Insulating Materials Sun Chencheng Hu Zijun Wang Qin Lu Sheng Chen Haikun （National Key Laboratory of Advanced Functional Composite Materials, Aerospace Research Institute of Materials Processing Technology, Beijing 100076 ） Abstract Rigid thermal insulating materials(RTIM) were prepared from ceramic fibers through sintering. The effects of density, fiber orientation, test temperature and compositing process on the mechanical properties of the RTIM were investigated. The results indicated that the mechanical properties of RTIM increased with the increasing of the density. Tensile and compressive properties of TRIM in plane direction were four times larger than that of in thickness direction. The compressive properties of TRIM at 800℃ and 1000 ℃ are 90% and 50% of taht at room temperature, respectively. The compressive properties of composites increased by 35% after composited with aerogel，while the tensile properties of composites kept unchanged. Key words Rigid thermal insulating materials, Mechanical Properties 1 前言 随着高超声飞行器的发展，对高效隔热材料的需求越来越迫切。刚性隔热材料是发展最 早的一类隔热材料，美国从上个世纪八十年代开始从事刚性隔热材料的研究，至今发展了 LI 、FRCI 、HTP 、AETB 、BRI等系列[1~3]，为美国航天飞机和高超飞行器的发展发挥了重要 作用。我国也较早地开展刚性隔热材料的研制工作，取得了长足的进展，性能达到了美国第 三代陶瓷瓦的性能水平。对于隔热材料首先关注的是材料的隔热性能，但力学性能也至关重 要的。本文从材料密度、纤维取向、测试温度和复合工艺等方面对刚性隔热材料的力学性能 进行了研究。 2 实验 2.1 材料的制备 按比例称取陶瓷纤维 1，陶瓷纤维 2 ，粘结剂，烧结剂在分散液中搅拌均匀，经抽滤成 型、干燥、烧结后制备出刚性隔热材料。刚性隔热材料与二氧化硅溶胶复合、老化、置换、 干燥后制备出复合气凝胶的刚性隔热