地聚物基无机涂层抗裂性能研究.pdfVIP

地聚物基无机涂层抗裂性能的研究 刘海锋，崔学民, 李娟，陈拥军 （广西大学化学与化工学院，广西南宁邮编530004 ） 摘要：以地聚物材料为原理研制的无机建筑涂层容易出现涂层开裂现象。本文用无机材料断裂理论分析了本无机 涂层开裂的影响因素。并针对开裂的原因提出了较好的解决途径：如可以采用细化原料、减小涂层厚度、加入有 机聚合物物形成无机－有机杂化复合材料以增强涂层韧性、加入纳米 ZnO 吸收涂层内外微应力等，通过这些手 段大大改善了无机涂层的性能，较好的解决了涂层开裂问题。 关键词：无机涂层；开裂；碱激发 中图分类号：□□□□□□ 文献标识码：A 文章编号： Study on anti-crack property of inorganic coatings based on geopolymer Haifeng Liu, Xuemin Cui, Juan Li, Yongjun Chen （School of Chemistry and Chemical Engineering, Guangxi University, Nanning 530004, P.R.China ） Abstract ：Building coating that prepared with geopolymer can easily develop crack when it is applied, this article analyzes the reasons of crack of our inorganic coating with inorganic material crack theory, in addition, we bring forward to the better approaches that can solve the problem of coating crack ：e.g. apply to smaller particle size of powders, decrease thickness of coating, add organic polymer into the inorganic coatings and become organic-inorganic hybrid coatings, increase the rates of absorbing stress of coatings by adding nano-ZnO particles. We improved capability of the coatings anti-crack through these methods, and solved the crack problems of the inorganic coatings. Key words ：inorganic coatings ；coatings crack ；alkali-actived 大大的影响了其实际应用，因此，我们通过研究理 引 言 论和大量实验，分析了该涂层开裂的原因。 无机涂料具有无毒、绿色环保、耐候性强、遇 1 实验过程和结果 火不燃烧、施工过程操作简便、高固份含量以及原 料来源广泛等优点，近些年来成为各国重点研究的 1.1 原料 方向[1] 。我国研究者和工程技术人员也花了大量的 表1 高岭土和偏高领土组成（wt% ） 人力和物力来开发新型无机涂料。我们以无机地聚 Table 1 Conten of kaolin and metakaolin (wt%)