锂离子电池过充保护剂地研究.pdfVIP

锂离子电池过充保护剂的研究 刘强，唐致远, 陈玉红,贺艳兵 （天津大学化工学院应用化学系，天津 300072） 摘要：本文对比分析了环己苯以及噻吩衍生物对锂离子电池过充安全性能的影响。作者采用交流阻抗和循环 伏安等电化学测试方法研究了几种添加剂的电化学行为。同时通过过充试验研究了含有添加剂的锂离子电池 在过充情况的下的行为。并得出结论：CHB 有着合适的保护电位和一定的耐过充能力；2，5－二氯噻吩对电 池的过充安全性影响较小；3－甲基噻吩不适于锂离子电池的过充保护。 关键词：过充保护；环己苯；噻吩衍生物 The Research of Overcharge Protection Additives for Lithium-ion Batteries TangZhiyuan, LiuQiang ,ChenYuhong,HeYanbing (Department of Applied Chemistry, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072) Abstract ：This essay compares and analyzes the effect of cyclohexyl benzene （CHB ）and thiophene deratives as the overcharge protection additives on the lithium ion batteries. Through the electrochemical impedance spectroscopy and cyclic voltammetry, the writer tested the electrochemical performance of these additives. Through the 1C overcharge testing, the writer study the overcharge performance of the lithium ion batteries that contain these additives. The writer concludes that CHB is suitable for the lithium ion overcharge protection; the 2.5-dichrolo thiophene has little effect on the over charge protection; 3-methyl thiophene is not suitable for lithium ion batteries. 锂离子电池自身的安全隐患[1]是限制锂离子电池使用范围，阻碍其在动力电池界推广的 主要原因。因此如何提高锂离子电池的安全性能成为一个迫在眉睫的问题。 有研究[2－6]表明电聚合物添加剂是一种有效的过充保护方法。这种添加剂可以在锂离子电 池被过充时发生聚合，从而对电池起到保护的作用。有专利研究环己苯 CHB 和噻吩衍生物可 收稿日期：2006-8-22 作者简介：唐致远（1946－），男（汉族），安徽定远人，天津大学化工学院教授，博士生导师， 研究方向：新型化学能源。电话：022 ，E-mail: zytang@tju.edu.cn 以作为电聚合物添加剂对锂离子电池进行过充保护，本文在此基础上研究对比了环己苯，3－ 甲基噻吩，2，5－二氯噻吩作为添加剂对锂离子电池安全性的影响。 1 实验 用水溶解质量配比为 3％羧甲基纤维素钠(CMC)＋6％聚苯乙烯丁橡胶（SBR）＋91％复合 石墨制成负极浆料，然后在铜箔上拉浆制成极片作为负极；用 N-甲基吡咯烷酮(NMP)溶解质量 配比为 90％Li2CoO2＋5％的导电石墨＋5％PVDF