异步交叉轧制能耗特性研究 赵　林　金国田　傅作宝　　　白光润 (鞍山钢铁(集团)公司)　　　(东北大学) 摘　要　对异步交叉轧制的能耗特性进行了分析与实验验证。研究表明，随交叉角增大，轧制能耗下降，当交叉角(θ)增至临界值(θcr)时，能耗最小，交叉角θ＞θcr后，能耗基本不变；随异步比增大，能耗亦下降，当异步比(i)增至临界值(icr)时，能耗最小， i＞icr后，能耗则上升，且θ愈大， icr亦愈大。即当交叉角为θcr且异步比亦为icr时，异步交叉轧制综合能耗最小。关键词　异步交叉轧制　异步比　交叉角　轧制能耗 STUDY ON ENERGY CONSUMPTION IN ASYMMETRIC AND CROSS ROLLING ZHAO Lin　JIN Guotian　FU Zhuobao (Anshan Iron Steel(Group) Co.) BAI Guangrun (Northeastern University)ABSTRACT　Based on the analysis of energy consumption (EC) characteristics of asymm-etric and cross rolling,it is shown that with the increase of cross angle θ,EC drops,and at a critical angle θcr,EC reaches a minimum when θ＞θcr，EC changes little.When speed ratio i increases,EC drops too, as i reaches to a critical value ratio icr, EC has a minimum value too, but when i＞icr，EC increases with i,and the larger θ the greater icr is.When θ＝θcr and i＝icr，the comprehensive energy consumption is the smallest.KEY WORDS　asymmetric and cross rolling,speed ratio,cross angle,energy consumption of rolling 　　迄今许多板带轧制工艺及轧机如HC、CVC、PC等轧机，主要是从控制板形，提高轧制精度方面入手研究的；而对于轧制过程中一个非常重要的特性——能耗的研究则显得十分薄弱，尽管已有学者对异步轧制的能耗特性进行了研究［1］，但总的来看仍很少。本文对新近提出的一种新型板带轧制工艺——异步交叉轧制的能耗特性进行了较系统的研究。 1　理论分析 　　本文提及的异步交叉轧制工艺，是将异步轧制和交叉轧制两种方式有机结合为一体的轧制方式［2］。　　轧制能耗是指轧制过程中轧机所消耗的电机功率Nd，通过传动系统传给轧辊，轧辊所消耗功率即辊身功率为Ng。异步交叉轧制下辊功率与轧制能耗之间关系见图1。 Ng＝Ndηcosαcos(α+θ) (1) 式中　η——传动系统效率；? 　　θ——轧辊交叉角/(°)；　? 　α——传动轴倾角/(°)。　　由式(1)知，异步交叉轧制实际用于轧制区的辊身功率将小于电机功率，这是因为传动效率及轧辊 图 1　辊身功率Ng与轧制能耗Nd间关系Fig.1　Relation between roll power Ng and energyconsumption of rolling Nd交叉要损失一部分能量。　　令m＝cosαcos(α+θ)，则式(1)改为 Ng＝Ndηm 异步交叉轧制(简称AC轧制)能耗为 Nd＝Ng/(ηm)＝［M1ω1+M2ω2］/(ηm)＝［MΣ+M1(i-1)］ω2/(ηm) (2) 式中　M1、M2——各为快辊与慢辊轧制转矩；　?? ω1、ω2——各为快辊与慢辊角速度； i＝ω1/ω2；　MΣ＝M1+M2 常规轧制能耗为 Nd＝Ng/η＝(M1+M2)ωc/η＝CsMΣω2/η 　(3) 式中　M1、M2——上下工作辊轧制转矩； MΣ＝M1+M2 Cs＝(1+S2)/(1+Sc) (4) 式中　S2、Sc——各为异步交叉轧制慢速辊与常规轧制的前滑值。　　为分析异步交叉轧制的能耗特性，需与常规轧制进行比较。令比较系数为f f＝Nd/Nd＝m［MΣ/MΣ+M1(i-1)/MΣ］/Cs (5) 式中 MΣ＝2μRPc(1-2Zc) (6) MΣ＝2QWPcCμR(1-2Z) (7) R——工作辊半径； 　　Q＝P/Pc——P、Pc各为异步轧制和常规轧制的轧制力；