304L不銹鋼軋延組織之氫脆特性研究.pdfVIP

304L 不銹鋼軋延組織之氫脆特性研究 林育如，蔡履文 國立台灣海洋大學材料工程研究所 Hydrogen embrittlement susceptibility of rolled 304L stainless steel in H2S solution Yu-Ru Lin, and L.W. Tsay Institute of Materials Engineering, National Taiwan Ocean University 摘要 本研究主要探討 304L 不銹鋼板材在常溫滾軋、150℃加熱滾軋及滾軋試件 經敏化處理(650℃/1h)後，在飽和硫化氫(H S)溶液中之缺口拉伸性質研究。 2 缺口拉伸試驗結果顯示，由於氫補集區的增加，減緩氫擴散至缺口尖端塑性 區，使常溫滾軋後的試片相較於其它試片具有較高缺口強度、較低的缺口強度損 失率。敏化後試片中的麻田散鐵、差排密度以及滾軋所致之缺陷大量減少，而導 致氫補集位置數量減少。另外，晶界附近的應變誘發麻田散鐵相變態提供了氫快 速擴散的路徑，致使缺口強度損失率升高。 關鍵字：不銹鋼、氫脆、滾軋。 Abstract The effects of rolling and sensitization treatment on the hydrogen embrittlement susceptibility (HES) of 304L stainless steel (SS) were investigated. Hydrogen embrittlement susceptibility of the specimen was associated with the loss of notched tensile strength (NTS) in H2S solution. The results indicated the increase in beneficial trapping sites for hydrogen in cold-rolled 304L SS accounted for the high NTS and low HES as compared with other specimens. The lowered trapping sites for hydrogen along with the grain boundary martensite, which provided fast diffusion path for hydrogen in the specimen, resulted in increasing the HES of the sensitized specimen. Key words: stain steel, hydrogen embrittlement, rolling. 1. 前言 304L 不銹鋼為沃斯田鐵系不銹鋼，具有良好的機械性質及抗腐蝕性，而能 廣泛應用於航空、航海、石化、核能及汽車工業的設備及管路上。 而氫脆現象對材料延展性、斷裂強度具有極重要的引響力，當材料處於氫環 境中，會使得氫原子進入材料中造成脆化及機械性質下降， 故本研究特別針對 常使用於各設備管路上的材料─304L 不銹鋼，探討 304L 不銹鋼在 H2S 環境中， 氫原子對材料缺口拉伸的影響，並利用肥粒鐵量測儀的量測及其他實驗結果，得 知相變態對氫脆效應所產生的影響。 2. 實驗步驟 本實驗採用材料為厚度 6mm 之 304L 不銹鋼板材，其成分為 18%Cr 、8%Ni 、 0.018%C 、1.58%Mn 、0.37%Si 、0.032%P 、0.002%S 、0.045%N 、Balance Fe 。