2219铝合金板材形变热处理中预变形对微观组织和力学性能的影响_英文_.pdfVIP

Trans. Nonferrous Met. Soc. China 22(2012) s370−s375 Effect of pre-deformation on microstructure and mechanical properties of 2219 aluminum alloy sheet by thermomechanical treatment 1,2 1 1 1 2 2 AN Li-hui , CAI Yang , LIU Wei , YUAN Shi-jian , ZHU Shi-qiang , MENG Fan-cheng 1. National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001, China; 2. Capital Aerospace Machinery Company, Beijing 100076, China Received 28 August 2012; accepted 25 October 2012 Abstract: Thermomechanical treatment is usually used to achieve good mechanical properties and microstructure of metal materials. The effect of pre-deformation on the microstructure and mechanical properties of 2219 aluminum alloy sheet by TMT process was investigated. The studies show that the yield strength and tensile strength increase firstly and decrease with the increase of pre-deformation under a certain heat treatment condition and total deformation. The tensile strength of 2219 aluminum alloy sheet reaches the maximum value when the pre-deformation is about 2%. It is also found that the very fine Al2Cu appears inside the grain, which is the precipitated phase for the strengthening of the 2219 aluminium alloy. Key words: 2219 aluminum alloy; thermomechanical treatment (TMT); pre-deformation; precipitation strengthening; mechanical properties aluminium alloy and refine the precipitated phase of 1 Introduction alloys notab