Terfenol-D合金新型制备工艺地研究.pdfVIP

Terfenol-D合金新型制备工艺的研究 刘何燕 李养贤 赵书文 曲静萍 孟祥熙 河北工业大学材料学院，天津300130 摘 要：本文研究了采用环氧树脂胶作为粘结剂和Sn作为添加剂的低温瞬时烧结制备 Terfenol-D的工艺。研究结果表明采用这两种工艺制备的样品尽管磁致伸缩性能较合金材料略有下 降，但材料的脆性、抗氧化性及高频应用特性都得到明显改善。其中采用环氧树脂胶粘结法制备的 Tb0.27Dy0.73Fe2粘结体，当预应力为10MPa时，粘结棒材在磁场为450kA/m时达到1186ppm。以Sn 作为添加剂的低温瞬时烧结方法制备的Terfenol-D磁致伸缩值达到546ppm。 Terfenol-D；磁致伸缩；粘结法；低温瞬时烧结 TG146.14+5 StudyonthepreparationofTerfenol-Dalloy LiuHeyan LiYangxian ZhaoShenwen QuJingping MengXiangxi SchoolofMaterialScienceandEngineering,HebeiUniversityofTechnology,Tianjin300130 Abstract:Inthiswork,theTeffenol-Dcompositeispreparedbypolymer-bondingmethodand low-temperatureinstantaneoussinteringwithadditionofSn.Theresultsshowthatthebrittleness,oxidation resistanceandtheappliedpropertyinthehighfrequencyofTerfenol-Dcompositepreparedbythese methodsareimproved.Withtheappliedcompressivestressof10MPa,thelargemagnetostrictionof1186 ppmat450kA/mforTeffenol-Dcompositepreparedbypolymer-bondingmethod.Themagnetostrictionof 546ppmat950kA/misobtainedforthesinteredcompactfabricatedbylow-temperatureinstantaneous sintering. Keywords:Terfenol-D;magnetostriction;polymer-bondingmethod;low-temperatureinstantaneous sintering @园 2006航空宇航科学与技未全国博士生学术论坛 2006年9月 独特的优点，粘结法制备工艺简单，可以制备大 Tbo．zTDyo．73Fe2的磁致伸缩曲线(样品的成形压 尺寸，及形状复杂的样品，此外，粘结法最突出 力为80MPa，胶与磁粉的质量比为6：100)。由 的优点是由于胶可以在颗粒的表面形成一层绝 图l可见，预应力大大提高了材料的磁致伸缩， 缘层，使粘结体的电阻率提高了几个量级，克服 了Terfenol—D合金电阻率低，在高频应用时，涡的1186 ppm，然而在测量磁场范围内，磁致伸 流损耗严重的难题。尽管采用制各薄板材料而后 缩并不是随压力的增加而单调增加的，预应力高 叠合在一起的方法也可以提高材料的电阻率，然 于12MPa，磁致伸缩反而降低，这是由于预应 而Terfen01．D合金非常脆，不利于加工，材料的力越大，由应力而产生的各向异性能也越大，在 自身特点使这种方法工艺复杂价格昂贵，并且采 相同的磁场下，磁畴越不容易转向磁场的方向， 用这种方法仅将材料的使用频率提高到20KHz。磁致伸缩也越小。 而采用粘结法18,9