榆钢 150mm 断面连铸方坯的二冷配水优化 ·1 · 榆钢 150mm 断面连铸方坯的二冷配水优化 田 陆 梁维盛 崔广礼 （镭目公司北京研究所，北京 100080 ） 摘 要 本文介绍榆钢方坯 2 号连铸机二冷配水系统的改造过程。针对榆钢公司方坯 2 号机的漏钢、裂纹等质量缺 陷和二冷配水不均匀的问题，对二冷室重新布置，新设计了0 段水环和二冷分区，调整各区冷却长度，更换了喷嘴 型号，对二冷配水参数进行了优化和调整后，拉速由原来的 2.4m/min 提升到 3.2m/min，铸坯内部质量合格，铸坯 外形明显得到提高。 关键词 二次冷却 比水量 配水 优化 Optimizing of Secondary Cooling System for a 150mm Billet CCM at Yuzhong Steel Tian Lu Liang Weisheng Cui Guangli (Beijing Research Institute, RAMON Science Technology, Co., Ltd., Beijing, 100080) ＆ Abstract This paper introduces the revamping project of Secondary Cooling System of No.2 Billet CCM (continuous casting machine) at Yuzhong Steel. In order to solve the problems of NO.2 billet CCM, such as breakout, crack uneven water cooling, we have redesigned the layout of secondary cooling system of No. 2 Billet CCM, redesigned collecting ring of 0 zero, changed the nozzle type and cooling length. After the optimizing and adjusting the parameters of the secondary cooling system, the casting speed is increased from 2.4m/min to 3.2m/min. Finally the billet internal soundness or profile quality is improved dramatically. Key words secondary cooling, specific water flow, secondary water distribution system, optimization 1 引言 酒钢榆钢公司连铸 2 号机于 2004 年投产，投产后的拉速一直维持在 2.0~2.4m/min 。随着运行时间的增 加，连铸坯的质量问题逐渐显现出来，一个问题是铸坯离开结晶器铜管后漏钢，而且经常性出现脱方。二是 铸坯的中间裂纹比较突出，影响轧钢质量。 出于解决连铸坯的质量问题和扩大产能、提高拉速的需要，2013 年酒钢榆钢公司对 2 号机进行二冷配 水升级改造。本文就 2 号机二冷配水改造前后，就存在的问题和铸坯的状况进行讨论。 2 榆钢连铸主要技术参数和存在问题 榆钢连铸 2 号机其主要技术参数如表 1。 田陆，男，博士，高级工程师，从事炼钢连铸领域研究，ramontl@ ·2 · 第九届中国钢铁年会论文集