2010 中国铸造活动周论文集 耐蚀镁合金的研究现状及进展 杨明波，李 晖，胡红军 （重庆理工大学材料科学与工程学院，重庆 400050） 摘要：耐蚀镁合金作为有发展前途的镁合金，目前已引起国内外的广泛关注和高度重视，并进行了大量的 研究。本文综述了耐蚀镁合金的研究开发现状，尤其是降低杂质元素含量、添加合金元素和采用合适加工 工艺提高合金耐蚀性这几方面的进展，指出了目前还存在的问题，并对今后的发展进行了展望。 关键词：镁合金；耐蚀镁合金；腐蚀 Current Research Status and Development of Corrosion Resistance Magnesium Alloys Yang Ming-bo, Li Hui,Hu Hong-jun (Materials Science and Engineering College, Chongqing University of Technology, Chongqing 400050) Abstract: Corrosion resistance magnesium alloys is thought as a potential magnesium alloys series, at present, the research and development about this series alloys have received much attention all over the world, and consequently many researches have been carried out. In the paper, the latest research and development status of this series magnesium alloys, especially these methods of improving corrosion resistance, such as the decreasing of imprurity elements content, adding alloy elements and adopting appropriate process, were reviewed, and the existing problems and the development trendance were also analyzed and pointed out respectively. Key words: Magnesium alloys; corrosion resistance magnesium alloys; corrosion 镁合金作为最轻质的金属工程结构材料，因其具有比重轻、节能降耗、比强度比刚度高、阻尼减振降 燥能力强、液态成形性能优越、能屏蔽电磁辐射和易于回收利用等一系列符合“21 世纪绿色结构材料”的 特征，使其特别适合于汽车、摩托车等交通工具和计算机、通讯、仪器仪表、家电、轻工、军事等领域的 应用。目前，尽管镁合金在世界汽车工业中的应用正以每年约 15～20%的速度快速增长，远远高于其它金 属材料。但总的来讲，其作为结构材料的应用潜力与现实之间仍然存在巨大反差，而造成这一现状的一个 重要原因就是镁合金的腐蚀问题，即较差的腐蚀性是制约镁合金发挥应用潜力的瓶颈问题之一。也正是看 到镁合金腐蚀防护问题的解决对于镁合金应用的推动作用，所以国内外对镁合金腐蚀防护问题的研究给予 了广泛关注和高度重视。近 10 多年来，国内外围绕镁合金的表面处理和耐蚀镁合金的开发等开展了大量 的研究工作，并取得了许多积极的成果[1～3]。但众所周知，表面处理只是被动对镁合金的腐蚀进行防护， 无法从根本上解决镁合金的腐蚀防护问题。因此，积极探索增强镁合金耐腐蚀性能的各种途径，并在此基 础上研究开发高性能耐蚀镁合金，对于从根本上解决镁合金的腐蚀问题，进而推动镁合金作为结构材料的 应用并充分发挥其性能优势具有非常重要的作用。 1 镁合金的主要腐蚀类型 总体而言，导致镁合金腐蚀性能下降的原因主要有以下两个：一是镁合金表面形成的 MgO 不能形