消失模铸造涂料性能控制与应用.pdfVIP

消失模铸造涂料的性能控制及应用 黄爱明 （上海欧区爱国际贸易有限公司，上海，201600 ） 摘要：消失模涂料在消失模工艺中起着极为重要的作用，一旦铸造工艺所需的涂料 被选定，制定一套稳定一致的监控程序是获得优质铸件的必要条件。涂料强度、耐 火度、悬浮性、固体含量及透气性等会对铸件质量产生巨大影响，只有使用恰当手 段将这些指标控制在合适的范围内，性能优异的涂料才能发挥出其最佳的性能。同 时，严格一致的涂料现场使用工艺也是极为重要的，这些程序包括涂料搅拌槽的清 洁、涂料的预混、温度控制和涂料性能参数测试等。 summary: As lost foam coating plays a very important role in the lost foam process. Once the coating has been selected, its necessary to fomulate a set of consistent monitor program for high quality castings. Casting quality is great affected by coating properties, such as coating strengh, refractoriness, suspension, solid content, gas permeability and so on. Only using proper method to control these data in suitable range, the coating could appear the best performance. At the same time, strictly consistent process of coating application is also extremely important, which includes mixing tank cleaning, coating pre-mix, temperature control and coating properties data testing, etc. 关键字：消失模涂料 质量控制 应用 Key words: lost foam coating, quality control, application 1、简介 消失模铸造是将与铸件尺寸形状相似的泡沫模型涂刷专用耐火涂料并烘干后， 埋在干砂中振动造型，然后浇注，高温液态金属使模型液化和气化，并快速占据泡 沫模型原来的位置，凝固冷却后形成铸件。由于其固有的特点，该方法获得的铸件 表面光洁度高于常用的传统粘土砂铸造和砂型铸造，不需要制芯，不用分型，造型 砂不用粘结剂，容易清理，对环境友好，可用于铸造发动机缸体缸盖等复杂铸件。 2、消失模铸造发展简史 1958 年，美国的H.F.Shroyer 发明了用可发性泡沫模样制造金属铸件的技术并取 得了专利，最初所用的模样是采用聚苯乙烯板材加工制成的，采用粘土砂造型，用 来生产艺术品铸件。采用这种方法，造型后泡沫模型不用取出，而是在浇入液态金 属后燃烧、分解而“让出”空间充满金属液，凝固后形成铸件。1961 年德国的Grunzweig 和Harrtmann 公司购买了这一专利加以开发，并于1962 年在工业上得到应用。采用 无粘结剂干砂生产铸件的技术由德国的H.Nellen 和美国的T.R.Smith 与1964 年申请了 专利。由于无粘结剂的干砂在浇注过程中经常发生坍塌等现象，所以1967 年德国的 A.Wittemoser 采用了可以被磁化的铁丸来代替硅砂作为造型材料，用磁力场作为“粘 结剂”，这就是所谓的“磁型铸造”。然而由于磁性铸造的造型机限制了产品的大小 和复杂程度，而且工序复杂，难于实现大批量自动化生产。1971 年日本的 Nagano 发明了真空铸造法，他采用无粘结剂的干砂作为造型材料，用抽真空的办法固定砂 型来形成型腔浇注铸件。受此方法的启发，今天的消失模铸造在很多地方也采用了 抽真空的办法来固定砂型。 3、消失模涂料在消失模工艺中的重要作用 涂料在消失模铸造工艺中的作用应该基于涂料在浇注过程中